Unprecedented Integral-Free Debye Temperature Formulas: Sample Applications to Heat Capacities of ZnSe and ZnTe
Table 2
Smoothed values of the isobaric
lattice heat capacities,
, and of the corresponding (effective) Debye temperatures,
(due to (
27) and (
28)).
| | ZnSe | ZnSe | ZnTe | ZnTe | (K) | (J⋅K−1 mol−1) | (K) | (J⋅K−1 mol−1) | (K) |
| 2 | 0.0015949 | 269.16 | 0.0029434 | 219.43 | 4 | 0.013255 | 265.76 | 0.025043 | 214.98 | 6 | 0.048985 | 257.84 | 0.10158 | 202.19 | 8 | 0.13589 | 244.67 | 0.31540 | 184.80 | 10 | 0.32260 | 229.26 | 0.75959 | 172.32 | 12 | 0.65875 | 216.85 | 1.44623 | 166.75 | 14 | 1.15330 | 209.86 | 2.3390 | 165.39 | 16 | 1.78730 | 207.06 | 3.3764 | 166.53 | 18 | 2.5396 | 206.75 | 4.4832 | 169.36 | 20 | 3.3793 | 208.10 | 5.6015 | 173.32 | 25 | 5.6132 | 216.48 | 8.3098 | 185.43 | 30 | 7.7928 | 228.48 | 10.903 | 197.66 | 35 | 9.9059 | 240.78 | 13.439 | 208.50 | 40 | 12.002 | 251.94 | 15.931 | 217.65 | 45 | 14.096 | 261.58 | 18.361 | 225.22 | 50 | 16.176 | 269.74 | 20.704 | 231.40 | 55 | 18.221 | 276.58 | 22.938 | 236.40 | 60 | 20.210 | 282.27 | 25.045 | 240.41 | 65 | 22.125 | 287.00 | 27.014 | 243.60 | 70 | 23.952 | 290.91 | 28.841 | 246.12 | 75 | 25.682 | 294.13 | 30.525 | 248.07 | 80 | 27.309 | 296.78 | 32.071 | 249.57 | 85 | 28.832 | 298.95 | 33.485 | 250.68 | 90 | 30.251 | 300.72 | 34.775 | 251.47 | 95 | 31.569 | 302.14 | 35.950 | 251.99 | 100 | 32.790 | 303.28 | 37.021 | 252.28 | 110 | 34.964 | 304.85 | 38.822 | 252.29 | 120 | 36.819 | 305.68 | 40.429 | 251.69 | 130 | 38.401 | 305.94 | 41.721 | 250.58 | 140 | 39.755 | 305.73 | 42.807 | 249.01 | 150 | 40.916 | 305.14 | 43.727 | 247.01 | 160 | 41.917 | 304.19 | 44.512 | 244.57 | 170 | 42.784 | 302.91 | 45.188 | 241.67 | 180 | 43.540 | 301.31 | 45.774 | 238.29 | 190 | 44.203 | 299.38 | 46.288 | 234.38 | 200 | 44.787 | 297.12 | 46.740 | 229.88 | 220 | 45.766 | 291.54 | 47.503 | 218.84 | 240 | 46.522 | 284.38 | 48.122 | 204.41 | 260 | 47.197 | 275.36 | 48.640 | 185.43 | 280 | 47.735 | 264.13 | 49.083 | 159.77 | 300 | 48.194 | 250.18 | 49.471 | 122.68 | 350 | 49.100 | 197.64 | 50.283 | — | 400 | 49.792 | 77.81 | 50.961 | — | 450 | 50.363 | — | 51.573 | — | 500 | 50.863 | — | 52.153 | — | 550 | 51.321 | — | 52.722 | — | 600 | 51.757 | — | 53.293 | — |
|
|