Abstract
Polycrystalline zinc oxide (ZnO) films were prepared by radio frequency (RF) magnetron
sputtering under different powers. The XRD results showed that ZnO crystallite size along
c-axis decreased by 43% with deposition power increased from 60 W
to 300 W, increased 36% with annealing temperature rising to