Synthesis and Characterization of High-Entropy Alloy FeCoNiCuCr by Laser Cladding
Table 1
The atomic composition and distribution in different
values.
| Alloy | Zone | at% | Al | Cr | Fe | Co | Ni | Cu |
| Al1.0FeCoNiCuCr | Nominal | 16.66 | 16.66 | 16.66 | 16.66 | 16.66 | 16.66 | Actual | 5.95 | 11.34 | 40.16 | 11.83 | 12.82 | 17.94 | DR | 5.64 | 12.42 | 42.36 | 12.94 | 11.70 | 14.94 | ID | 6.91 | 11.61 | 44.18 | 14.18 | 10.58 | 12.53 |
| Al1.3FeCoNiCuCr | Nominal | 20.63 | 15.87 | 15.87 | 15.87 | 15.87 | 15.87 | Actual | 14.84 | 16.28 | 23.93 | 15.68 | 15.71 | 13.46 | DR | 15.29 | 17.47 | 25.63 | 17.71 | 14.20 | 9.71 | ID | 16.46 | 16.97 | 21.67 | 14.22 | 16.16 | 14.53 |
| Al1.5FeCoNiCuCr | Nominal | 23.08 | 15.38 | 15.38 | 15.38 | 15.38 | 15.38 | Actual | 14.30 | 17.84 | 23.61 | 15.75 | 15.12 | 13.38 | DR | 14.78 | 20.69 | 27.70 | 16.56 | 11.34 | 8.93 | ID | 10.99 | 15.85 | 25.96 | 15.40 | 15.79 | 16.01 |
| Al1.8FeCoNiCuCr | Nominal | 26.47 | 14.71 | 14.71 | 14.71 | 14.71 | 14.71 | Actual | 20.99 | 14.92 | 16.36 | 16.28 | 14.65 | 16.80 | DR | 19.10 | 15.66 | 22.73 | 17.89 | 14.53 | 10.10 | ID | 20.41 | 14.73 | 18.57 | 13.81 | 16.66 | 15.82 |
| Al2.0FeCoNiCuCr | Nominal | 28.57 | 14.29 | 14.29 | 14.29 | 14.29 | 14.29 | Actual | 17.06 | 13.68 | 21.52 | 16.28 | 15.12 | 16.34 | DR | 17.89 | 12.68 | 27.62 | 13.57 | 14.92 | 13.32 | ID | 5.63 | 13.58 | 25.88 | 15.51 | 20.19 | 19.21 |
|
|