Effect of Induced Charge on the Passivity and Passivity Breakdown of 304LN Stainless Steels
Table 4
Corrosion data with and without induced charge above pitting potential.
| Sample | () | (mA/cm2) |
| Without charge in 0.15N KCl solution | −0.25 | 0.23 | With positive charge in 0.15N KCl solution | −0.35 | 0.28 | With negative charge in 0.15N KCl solution | −0.35 | 0.42 | Without charge in 0.2N KCl solution | −0.4 | 0.49 | With positive charge in 0.2N KCl solution | −0.36 | 0.38 | With negative charge in 0.2N KCl solution | −0.3 | 0.62 | Without charge in 0.25N KCl solution | −0.35 | 0.61 | With positive charge in 0.25N KCl solution | −0.25 | 0.3 | With negative charge in 0.15N KCl solution | −0.3 | 0.68 |
|
|