Effect of Induced Charge on the Passivity and Passivity Breakdown of 304LN Stainless Steels

Table 6

EIS data in 0.2N KCl solution.

Samples values values AlphaModel type

Below pitting potential without charge4.372e32.6712.48.5e−6678.7e−3CPE
Below pitting potential with positive charge5.103e32.499345.1e−6662.8e−3CPE
Below pitting potential with negative charge2.926e32.425371.7e−6643.0e−3CPE
Above pitting potential without charge1.553e32.493434.9e−6623.8e−3CPE
Above pitting potential with positive charge6.808e3572.6e−3325.5e−6652.3e−3CPE
Below pitting potential with negative charge888.82.838648.2e−6561.6e3CPE

We are committed to sharing findings related to COVID-19 as quickly and safely as possible. Any author submitting a COVID-19 paper should notify us at help@hindawi.com to ensure their research is fast-tracked and made available on a preprint server as soon as possible. We will be providing unlimited waivers of publication charges for accepted articles related to COVID-19.