| Glasses | Heat treatment temperature (°C) | Crystalline phases |
| LD1 | 700 | Li2Si2O5, Li2SiO3, Li0.6Al0.6Si2.4O6, Li3PO4, Ca5(PO4)3F, SiO2 | 750 | Li2Si2O5, Li2SiO3, Li0.6Al0.6Si2.4O6, Li3PO4, Ca5(PO4)3F, SiO2 | 800 | Li2Si2O5, Li2SiO3, Li0.6Al0.6Si2.4O6, Li3PO4, Ca5(PO4)3F | 850 | Li2Si2O5, Li2SiO3, Li0.6Al0.6Si2.4O6, LiAlSi2O5, Li3PO4, Ca5(PO4)3F |
| LD2 | 700 | Li2Si2O5, Li2SiO3, Li0.6Al0.6Si2.4O6, Li3PO4, Ca5(PO4)3F, SiO2 | 750 | Li2Si2O5, Li2SiO3, Li0.6Al0.6Si2.4O6, Li3PO4, Ca5(PO4)3F | 800 | Li2Si2O5, Li2SiO3, Li0.6Al0.6Si2.4O6, Li3PO4, Ca5(PO4)3F | 850 | Li2Si2O5, Li2SiO3, Li0.6Al0.6Si2.4O6, Li3PO4, Ca5(PO4)3F |
| LD3 | 700 | Li2Si2O5, Li2SiO3, Li0.6Al0.6Si2.4O6, Li3PO4, Ca5(PO4)3F, SiO2 | 750 | Li2Si2O5, Li2SiO3, Li0.6Al0.6Si2.4O6, Li3PO4, Ca5(PO4)3F | 800 | Li2Si2O5, Li2SiO3, Li0.6Al0.6Si2.4O6, Li3PO4, Ca5(PO4)3F | 850 | Li2Si2O5, Li2SiO3, Li0.6Al0.6Si2.4O6, Li3PO4, Ca5(PO4)3F |
| LD4 | 700 | Li2Si2O5, Li2SiO3, Li0.6Al0.6Si2.4O6, Li3PO4, Ca5(PO4)3F, SiO2 | 750 | Li2Si2O5, Li2SiO3, Li0.6Al0.6Si2.4O6, Li3PO4, Ca5(PO4)3F | 800 | Li2Si2O5, Li2SiO3, Li0.6Al0.6Si2.4O6, Li3PO4, Ca5(PO4)3F | 850 | Li2Si2O5, Li2SiO3, Li0.6Al0.6Si2.4O6, Li3PO4, Ca5(PO4)3F |
|
|