Effect of Casting Parameters on the Microstructural and Mechanical Behavior of Magnesium AZ31-B Alloy Strips Cast on a Single Belt Casting Simulator
Table 6
Mechanical properties of AZ31-B strips.
| Substrate no. | Depth of groove (mm) | Thickness | Coating | Heat flux | Rc | HV | YS | TS | W/m2 °C × 10−4 | MPa | MPa |
| III (c) | 0.15 | 3 mm | No | 6.6 | 4.545 | 62 | 147 | 166.6 | II (b) | 0.09 | 3 mm | No | 5.77 | 5.195 | 61 | 144 | 163.2 | IV (d) | 0.24 | 3 mm | No | 5.17 | 5.797 | 60 | 144 | 163.2 | I (a) | 0 | 3 mm | No | 5.06 | 5.927 | 58 | 141 | 159.8 | V (e) | 0.3 | 3 mm | No | 4.37 | 6.857 | 56 | 138 | 156.4 | VI (f) | 0.6 | 3 mm | No | 3.35 | 8.955 | 54.5 | 135 | 153 |
| III (c) | 0.15 | 3 mm | Yes | 3.5 | 8.571 | 54.9 | 135 | 153 | II (b) | 0.09 | 3 mm | Yes | 3.2 | 9.375 | 54.2 | 135 | 153 | IV (d) | 0.24 | 3 mm | Yes | 2.9 | 10.345 | 53.1 | 132 | 149.6 | I (a) | 0 | 3 mm | Yes | 2.85 | 10.526 | 50.7 | 141 | 159.8 | V (e) | 0.3 | 3 mm | Yes | 2.5 | 11.628 | 50.2 | 141 | 159.8 | VI (f) | 0.6 | 3 mm | Yes | 2.5 | 12.000 | 50 | 141 | 159.8 |
| III (c) | 0.15 | 1 mm | Yes | 2.5 | 4.000 | 49.8 | 126 | 142.8 | II (b) | 0.09 | 1 mm | Yes | 2.33 | 4.292 | 48.4 | 126 | 142.8 | IV (d) | 0.24 | 1 mm | Yes | 2.16 | 4.617 | 48.2 | 126 | 142.8 | I (a) | 0 | 1 mm | Yes | 2.12 | 4.717 | 48.1 | 126 | 142.8 | V (e) | 0.3 | 1 mm | Yes | 1.83 | 5.464 | 48 | 126 | 142.8 | VI (f) | 0.6 | 1 mm | Yes | 1.72 | 5.814 | 47.9 | 123 | 139.4 |
|
I |
0 (steel) |
3 mm | No | 1.2 | 25.000 | 47.5 | 123 | 139.4 | Yes | 0.71 | 42.254 | 47 | 123 | 139.4 |
|
|