Corrosion Behavior of Pure Cr, Ni, and Fe Exposed to Molten Salts at High Temperature

<table>Electron image of the metal-scale interface and X-ray mappings of Fe, O, and V when pure metal iron was exposed to NaVO<sub>3</sub> at 700°C during 100 hours.</table>