Effect of Silicon Addition on High-Temperature Solid Particle Erosion-Wear Behaviour of Mullite-SiC Composite Refractories Prepared by Nitriding Reactive

<table>SEM photographs and EDS spectrum of samples: (a) surface fracture microstructure of sample M4; (b) surface microstructure of sample M4; (c) EDS spectrum of point A in (b).</table>

Advances in Materials Science and Engineering

fig2

Figure 2

Figure 2: Effect of Silicon Addition on High-Temperature Solid Particle Erosion-Wear Behaviour of Mullite-SiC Composite Refractories Prepared by Nitriding Reactive 

Figure 2 | Effect of Silicon Addition on High-Temperature Solid Particle Erosion-Wear Behaviour of Mullite-SiC Composite Refractories Prepared by Nitriding Reactive 