Effect of Silicon Addition on High-Temperature Solid Particle Erosion-Wear Behaviour of Mullite-SiC Composite Refractories Prepared by Nitriding Reactive

<table>Erosion morphologies of the aggregate and binder phases in the samples: (a) sample M1 (no silicon added) eroded at 25°C; (b) sample M4 (12% silicon added) eroded at 25°C; (c) sample M4 (12% silicon added) eroded at 800°C.</table>

Advances in Materials Science and Engineering

fig4

Figure 4

Figure 4: Effect of Silicon Addition on High-Temperature Solid Particle Erosion-Wear Behaviour of Mullite-SiC Composite Refractories Prepared by Nitriding Reactive 

Figure 4 | Effect of Silicon Addition on High-Temperature Solid Particle Erosion-Wear Behaviour of Mullite-SiC Composite Refractories Prepared by Nitriding Reactive 