Effect of Silicon Addition on High-Temperature Solid Particle Erosion-Wear Behaviour of Mullite-SiC Composite Refractories Prepared by Nitriding Reactive

<table>Representative SEM photography shows plastic deformation of samples: (a) sample M1 (no silicon added) eroded at 1200°C and (b) sample M4 (12% silicon added) eroded at 1200°C.</table>