Advances in Materials Science and Engineering
Volume 2014 (2014), Article ID 943542, 8 pages
http://dx.doi.org/10.1155/2014/943542
Research Article

Effect of Silicon Addition on High-Temperature Solid Particle Erosion-Wear Behaviour of Mullite-SiC Composite Refractories Prepared by Nitriding Reactive

1School of Materials Science and Technology, National Laboratory of Mineral Materials, China University of Geosciences (Beijing), Beijing 100083, China
2Key Laboratory on Deep Geodrilling Technology of the Ministry of Land and Resources, China University of Geosciences (Beijing), Beijing 100083, China

Received 6 November 2013; Accepted 11 December 2013; Published 16 January 2014

Academic Editor: Majid R. Ayatollahi

Copyright © 2014 Xiaochao Li et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Linked References

  1. J. P. Bennett and K. S. Kwong, “Refractory liner materials used in slagging gasifiers,” Refractories Application and News, vol. 9, pp. 21–25, 2004. View at Google Scholar
  2. J.-Z. Yang, M.-H. Fang, Z.-H. Huang et al., “Solid particle impact erosion of alumina-based refractories at elevated temperatures,” Journal of the European Ceramic Society, vol. 32, no. 2, pp. 283–289, 2012. View at Publisher · View at Google Scholar · View at Scopus
  3. X. C. Li, Z. H. Huang, Y. G. Liu et al., “Effect of silicon addition on mechanical properties of mullite-SiC composite refractories,” Journal of the Ceramic Society of Japan, vol. 120, pp. 574–578, 2012. View at Google Scholar
  4. D.-S. Park, B.-D. Han, D.-S. Lim, and I.-W. Yeo, “A study on wear and erosion of sialon-Si3N4 whisker ceramic composites,” Wear, vol. 203-204, pp. 284–290, 1997. View at Google Scholar · View at Scopus
  5. J. T. Huang, Y. G. Liu, Z. H. Huang et al., “Ni(NO3)2-assisted catalytic synthesis and photoluminescence property of ultralong single crystal Sialon nanobelts,” Crystal Growth & Design, vol. 13, pp. 10–14, 2013. View at Google Scholar
  6. V. A. Izhevskiy, L. A. Genova, J. C. Bressiani, and F. Aldinger, “Progress in SiAlON ceramics,” Journal of the European Ceramic Society, vol. 20, no. 13, pp. 2275–2295, 2000. View at Publisher · View at Google Scholar · View at Scopus
  7. T. Ekström and M. Nygren, “SiAlON ceramics,” Journal of the American Ceramic Society, vol. 75, pp. 259–276, 1992. View at Google Scholar
  8. S. Kurama, M. Herrmann, and H. Mandal, “The effect of processing conditions, amount of additives and composition on the microstructures and mechanical properties of α-SiAlON ceramics,” Journal of the European Ceramic Society, vol. 22, no. 1, pp. 109–119, 2002. View at Publisher · View at Google Scholar · View at Scopus
  9. J. Huang, M. Fang, Y. Liu, and Z. Huang, “Preparation of β-Sialon from fly ash by carbothermal reduction-nitridation reaction,” Key Engineering Materials, vol. 368, pp. 910–912, 2008. View at Google Scholar · View at Scopus
  10. Z.-H. Huang, J.-Z. Yang, Y.-G. Liu et al., “Novel sialon-based ceramics toughened by ferro-molybdenum alloy,” Journal of the American Ceramic Society, vol. 95, no. 3, pp. 859–861, 2012. View at Publisher · View at Google Scholar · View at Scopus
  11. J. M. Ferreira and K. X. Chen, “Toughening Y α-sialon ceramics by using new-developed rod-like Y α-sialon crystals as reinforcing agents,” Key Engineering Materials, vol. 224, pp. 269–274, 2002. View at Google Scholar · View at Scopus
  12. M. I. Jones, K. Hirao, H. Hyuga, Y. Yamauchi, and S. Kanzaki, “Wear properties of Y-α/β composite sialon ceramics,” Journal of the European Ceramic Society, vol. 23, no. 10, pp. 1743–1750, 2003. View at Publisher · View at Google Scholar · View at Scopus
  13. M. I. Jones, H. Hyuga, K. Hirao, and Y. Yamauchi, “Wear behaviour of single phase and composite sialon ceramics stabilized with Y2O3 and Lu2O3,” Journal of the European Ceramic Society, vol. 24, no. 10-11, pp. 3271–3277, 2004. View at Publisher · View at Google Scholar · View at Scopus
  14. V. X. Lima Filho, J. P. Davim, C. A. Cairo, and J. M. F. Ferreira, “Preparation and characterization of SiAlON matrix composites reinforced with combustion synthesis rod-like SiAlON particles,” International Journal of Refractory Metals and Hard Materials, vol. 27, no. 3, pp. 647–652, 2009. View at Publisher · View at Google Scholar · View at Scopus
  15. K. X. Chen, J. Haibo, H. Zhou, and J. M. Ferreira, “Microstructure and formation mechanism of combustion-synthesized rodlike Ca α-sialon crystals,” Journal of Materials Research, vol. 16, no. 7, pp. 1928–1934, 2001. View at Google Scholar · View at Scopus
  16. K. Chen, M. E. F. L. Costa, H. Zhou, and J. M. F. Ferreira, “Novel rod-like yttrium α-sialon crystalline powders prepared by combustion synthesis,” Materials Chemistry and Physics, vol. 75, no. 1–3, pp. 252–255, 2002. View at Publisher · View at Google Scholar · View at Scopus
  17. R. Fu, K. Chen, X. Xu, and J. M. F. Ferreira, “Combustion synthesis of rod-like α-SiAlON seed crystals,” Materials Letters, vol. 58, no. 12-13, pp. 1956–1958, 2004. View at Publisher · View at Google Scholar · View at Scopus
  18. D. K. Shetty, A. R. Rosenfield, and W. H. Duckworth, “Mixed-mode fracture in biaxial stress state: application of the diametral-compression (Brazilian disk) test,” Engineering Fracture Mechanics, vol. 26, no. 6, pp. 825–840, 1987. View at Google Scholar · View at Scopus
  19. S. Dileep and D. K. Shetty, “Fracture toughness of polycrystalline ceramics in combined mode I and mode II loading,” Journal of the American Ceramic Society, vol. 72, no. 1, pp. 78–84, 1989. View at Google Scholar · View at Scopus
  20. D. Singh and D. K. Shetty, “Microstructural effects on fracture toughness of polycrystalline ceramics in combined mode I and mode II loading,” Journal of Engineering for Gas Turbines and Power, vol. 111, pp. 174–180, 1989. View at Google Scholar
  21. D. Singh and D. K. Shetty, “Subcritical crack growth in soda-lime glass in combined mode I and mode II loading,” Journal of the American Ceramic Society, vol. 7, pp. 3597–3606, 1990. View at Google Scholar
  22. S. Y. Yarema, G. S. Ivanitskaya, A. L. Maistrenko, and A. I. Zboromirskii, “Crack development in a sintered carbide in combined deformation of types I and II,” Strength of Materials, vol. 16, no. 8, pp. 1121–1128, 1984. View at Publisher · View at Google Scholar · View at Scopus
  23. S. Suresh, C. F. Shih, A. Morrone, and N. P. O'Dowd, “Mixed-mode fracture toughness of ceramic materials,” Journal of the American Ceramic Society, vol. 73, no. 5, pp. 1257–1267, 1990. View at Google Scholar · View at Scopus
  24. H. Awaji and T. Kato, “Griffith criterion for mode II fracture of ceramics,” in Proceedings of the 11th International Conference on Experimental Mechanics, pp. 1199–1204, Oxford, UK, 1998.
  25. M. R. Ayatollahi and M. R. M. Aliha, “Mixed mode fracture analysis of polycrystalline graphite—a modified MTS criterion,” Carbon, vol. 46, no. 10, pp. 1302–1308, 2008. View at Publisher · View at Google Scholar · View at Scopus
  26. M. R. M. Aliha and M. R. Ayatollahi, “On mixed-mode I/II crack growth in dental resin materials,” Scripta Materialia, vol. 59, no. 2, pp. 258–261, 2008. View at Publisher · View at Google Scholar · View at Scopus
  27. T. Machida and N. Isobe, “Evaluation of mixed-mode fracture toughness using cracked Brazilian disk,” Transactions of the Japan Society of Mechanical Engineers A, vol. 61, no. 592, pp. 2552–2559, 1995. View at Google Scholar · View at Scopus
  28. A. R. Rosenfield, “Fracture of brittle materials under a simulated wear stress system,” Journal of the American Ceramic Society, vol. 72, no. 11, pp. 2117–2120, 1989. View at Google Scholar · View at Scopus
  29. M. R. Ayatollahi and M. R. M. Aliha, “Mixed mode fracture in soda lime glass analyzed by using the generalized MTS criterion,” International Journal of Solids and Structures, vol. 46, no. 2, pp. 311–321, 2009. View at Publisher · View at Google Scholar · View at Scopus
  30. M. R. Ayatollahi and M. R. M. Aliha, “Fracture analysis of some ceramics under mixed mode loading,” Journal of the American Ceramic Society, vol. 94, no. 2, pp. 561–569, 2011. View at Publisher · View at Google Scholar · View at Scopus
  31. M. R. M. Aliha and M. R. Ayatollahi, “Analysis of fracture initiation angle in some cracked ceramics using the generalized maximum tangential stress criterion,” International Journal of Solids and Structures, vol. 49, pp. 1877–1883, 2012. View at Publisher · View at Google Scholar · View at Scopus
  32. V. Tikare and S. R. Choi, “Combined mode I-mode II fracture of 12-mol%-ceria-doped tetragonal zirconia polycrystalline ceramic,” Journal of the American Ceramic Society, vol. 80, no. 6, pp. 1624–1626, 1997. View at Google Scholar · View at Scopus
  33. M. Li and M. Sakai, “Mixed-mode fracture of ceramics in asymmetric four-point bending: effect of crack-face grain interlocking/bridging,” Journal of the American Ceramic Society, vol. 79, no. 10, pp. 2718–2726, 1996. View at Google Scholar · View at Scopus
  34. F. Liu, M. Fang, X. Wang, Y. Liu, and Z. Huang, “Solid particle erosion behavior of 3YSZ ceramics at elevated temperatures,” Key Engineering Materials, vol. 492, pp. 85–88, 2012. View at Publisher · View at Google Scholar · View at Scopus
  35. Z. H. Huang, J. L. Sun, J. X. Wang, and Y. R. Hong, “β-sialon-Al2O3-SiC composite refractories,” Key Engineering Materials, vol. 224, pp. 275–280, 2002. View at Google Scholar · View at Scopus
  36. J. B. Wachtman, W. R. Cannon, and M. J. Matthewson, Mechanical Properties of Ceramics, John Wiley & Sons, New York, NY, USA, 2009.
  37. E. Karamian and A. Monshi, “Influence of additives on nano-SiC whisker formation in alumina silicate-SiC-C monolithic refractories,” Ceramics International, vol. 36, no. 2, pp. 811–816, 2010. View at Publisher · View at Google Scholar · View at Scopus
  38. M. W. Barsoum and B. Houng, “Transient plastic phase processing of titanium-boron-carbon composites,” Journal of the American Ceramic Society, vol. 76, pp. 1445–1451, 1993. View at Google Scholar