Effect of Silicon Addition on High-Temperature Solid Particle Erosion-Wear Behaviour of Mullite-SiC Composite Refractories Prepared by Nitriding Reactive
Table 2
Properties of mullite-SiC composite refractories prepared by nitriding reactive.
Property
Samples
M1
M2
M3
M4
Bulk density (g/cm
3
)
2.12
2.15
2.19
2.27
Apparent porosity (%)
28.4
27.2
26.1
23.6
Cold compression strength (MPa), ≥
40
60
80
120
Cold bending strength (MPa)
17.30
24.58
29.96
40.08
Vickers hardness of binder phase (GPa)
8.7
9.5
10.4
11.9