Abstract

This study shows the structural characterization of silica particles extracted from Stenotaphrum secundatum (St. Augustine) grass using an annelid-based biotransformation process. This bioprocess starts when St. Augustine grass is turned into humus by vermicompost, and then goes through calcination and acid treatment to obtain silica particles. To determine the effect of the bioprocess, silica particles without biotransformation were extracted directly from the sample of grass. The characterization of the silica particles was performed using Infrared (FTIR) and Raman spectroscopy, Transmission Electron Microscopy (TEM), X-ray Diffraction (XRD), Dynamic Light Scattering (DLS), and Energy Dispersion Spectroscopy (EDS). Both types of particles showed differences in morphology and size. The particles without biotransformation were essentially amorphous while those obtained via annelids showed specific crystalline phases. The biological relationship between the metabolisms of worms and microorganisms and the organic-mineral matter causes changes to the particles' properties. The results of this study are important because they will allow synthesis of silica in cheaper and more ecofriendly ways.

1. Introduction

Of all plants, the grasses are the most important to man. All our breadstuffs, corn, wheat, oats, rye, barley, and rice, are grasses. The food, agricultural, and forestry industries produce large volumes of waste annually worldwide as by-products of use of these grasses, causing a serious disposal problem; however, they constitute a renewable resource from which many useful materials can be derived. In leaves of grasses, silica can constitute 2–5% dry matter, 10–20 times higher than levels found typically in dicotyledonous plants [1]. Silica is stored primarily as opaline phytoliths in the epidermis [2]. Although all plants rooting in soil contain some Si in their tissues [3], the content differs greatly between plant species because of differences in Si uptake by the roots. Uptake and translocation occur as monosilicic acid and the deposition form is amorphous silica gel SiO2·nH2O [4]. Accumulation of such high levels of a single mineral element within grasses family suggests that it has a functional significance. Progress in understanding the uptake and accumulation of Si in plants has been led extensively by some authors [58]. The opal-like phytoliths (hydrated amorphous silica) occur in the tissue of grasses in a three-dimensional distribution in such a way as to suggest that silica is being excluded from the cells and deposited as silica gel in the spaces between cells. The silica is transported as Si(OH)4 and then concentrated and gelled as water evaporates from the leaves. Pores in the gel measure between 1 and 10 nm in diameter and are full of water, making silica completely amorphous [9]. Precipitation and polymerization of the silica, aided by evaporation and water metabolism in the plant’s body, lead to the formation of intra- as well as extracellular silica bodies. Intracellularly, silica accumulates in both the cytoplasm and the vacuoles of the plant cells and can be deposited in roots, stem, and leaves. Earlier, our group reported the synthesis of nanoparticles of silica oxide from rice husk, sugar cane bagasse, and coffee husk, by employing vermicompost with annelids (Eisenia foetida) [10]. The characterization of these particles can contribute to the understanding of the natural mechanism of transformation from the amorphous form to nanocrystals oxides in intestines of the worms. This bioprocess can be applied in the use of waste grass to produce specific nanocrystals with potential applications in materials science.

St. Augustine grass (Stenotaphrum secundatum) is native to the coastal regions of the Gulf of Mexico and the Mediterranean. This specimen is widely used as a turf grass in warm, humid, tropical, and subtropical climates where its broad leaf blades produce a tight canopy from rapidly elongating stolons, resulting in a coarse-textured turf [11]. Adaptive and morphological variations in St. Augustine grass are associated with chromosome differences. The most conspicuous differences among ploidy levels are that diploids are lower growing and have narrower, translucent, bright green leaf blades while polyploids have coarser, thicker leaf blades that are blue/green and less saturated in colour [12]. Although commonly found on siliceous and calcareous sands near the sea, St. Augustine grass also grows on a wide range of well to poorly drained soils, from sandy loams to light clays. Silicon accumulation in dry land Gramineae such as St. Augustine grass has been reported to be between 0.5 and 1.5%, while in dicotyledons (i.e., broadleaf plants) it is less than 0.2%. Indeed, the amounts of silicon that plants accumulate from the soil can be much higher than the amounts of any other essential macro- or micronutrients [13].

Vermicompost is the excreta of earthworms, which are capable of improving soil health and nutrient status. Vermiculture is a process by which all types of biodegradable waste, such as farm wastes, kitchen wastes, market wastes, biowastes of agrobased industries, and livestock wastes, are converted while passing through the worm gut to nutrient rich vermicompost. Vermi worms are used here as biological agents to consume those wastes and to deposit excreta in the process called vermicomposting [14]. Vermicomposting is a simple biotechnological process of composting, in which certain species of earthworms are used to enhance the process of waste conversion and produce a better product. Vermicomposting is a mesophilic process that utilizes microorganisms and earthworms that are active at 10°C to 32°C (not ambient temperature but the temperature within the pile of moist organic material). The process is faster than composting because the material passes through the earthworm gut and a significant but not fully understood transformation takes place, whereby the resulting earthworm casting (worm manure) is rich in microbial activity. Earthworms have been long recognized by farmers as beneficial to soil [15] and, as one of the major soil macrofauna, constitute an important group of secondary decomposers. Earthworms are key biological agents in the degradation of organic wastes [16]. Each earthworm weighs about 0.5 to 0.6 g, eats waste equivalent to its body weight, and produces cast equivalent to about 50% of the waste it consumes in a day. These worm castings have been analysed for chemical and biological properties. The moisture content of castings ranges between 32% and 66% and the pH is around 7.0. The final product of vermicompost bioprocess is called humus and it could be considered a driving force in the varying nature of terrestrial ecosystems [17]. Humus differs from the nonhumic substances such as carbohydrates (a major fraction of soil carbon), fats, waxes, alkanes, peptides, amino acids, proteins, lipids, and organic acids by the fact that distinct chemical formulae can be written for these nonhumic substances. Most small molecules of nonhumic substances are rapidly degraded by microorganisms within the soil. In contrast, soil humus is slow to decompose (degrade) under natural soil conditions. In combination with soil minerals, soil humus can persist for several hundred years. Some of the most beneficial attributes of humus are associated with its ability to make small, inorganic particles adhere together as loose, friable aggregates. Earthworm activities determine the soils’ characteristics and take an active part in energy and nutrient cycling through the selective activation of both mineralization and humification processes [18].

Apparently, in earthworms the mineralization is biologically induced, which is described as a mostly unintentional consequence of metabolic activities in the microbial organism. The nanoparticles produced in this process are an extracellular by-product of the microbial metabolism. The bacteria or other types of microbe secrete organic products attract ions or compounds in their vicinity, which subsequently result in concentration, alteration, immobilization, or depletion of these minerals. This means that the formation of elemental crystals is not directly controlled by the microbe. This can produce random crystallization or a lack of specific crystal morphologies [19]. Minerals formed in this manner also tend to be impure in the crystal lattice and full of inclusions of other minerals and compounds [20]. Some works about biotransformation and the biomineralization process where earthworms are involved have been reported [21, 22]. In the earthworms intestine there exist a wide range of microorganisms, including bacteria, algae, protozoa, actinomycetes, fungi, and even nematodes, which are found commonly throughout the length of the earthworms gut. The species of microbes in the gut are usually very similar to those in the surrounding soil or organic matter upon which the earthworms feed. Earthworms are dependent upon range of microorganisms in their nutrition and probably fungi are the most important microbes as food. It seems likely that protozoa are also important in their diet but that bacteria and actinomycetes are much less important [23]. Several studies have showed that under certain conditions of pressure and temperature the biomineralization (silicification) can be induced in presence of microorganisms and demonstrated that a complex interplay exists between the precipitations of silica, texture, and structures formed [24].

This study shows the structural characterization of silica particles extracted from grass Stenotaphrum secundatum (St. Augustine) using an annelid-based biotransformation process. The aim was to investigate changes in the properties of these particles caused by the bioprocess, and we propose that these biostructures could be used for the synthesis of new materials in a cheap and ecofriendly manner.

2. Materials and Methods

The seed of St. Augustine grass (Stenotaphrum secundatum) (Walt.) Kuntze was obtained from a commercial source, planted in a garden, and grown for about 3 months. Once mowed, it was added to the vermicompost. The specimen of annelid used was Eisenia foetida. The environmental conditions ideal for the reproduction and control of these samples were set up: temperature at 20°C, moisture around 60–85%, aeration conditions, and darkness. The stabilization time was around 1 month and the humus obtained was dried at room temperature. Then, the humus was sieved to a size of approximately 0.5 mm. Next, the sample was calcinated for 19 h at a temperature of 500°C to eliminate the organic matter. Calcinations were carried out in a muffle Lindberg/Eurotherm model 847 with energy consumption of 0.17 kcal/h cm3, and then the samples were treated with nitric and hydrochloric acids (volume ratio 3 : 1). For each gram of sample calcinated, 4 mL of acid mix was added in order to eliminate impurities. Acid treatment was performed at 40°C for 4 h with constant stirring. Then, the sample was filtrated and washed with distilled water to neutralize it. Solids obtained were dried at room temperature. All reagents employed were provided by Sigma-Aldrich. Silica obtained from St. Augustine grass without the bioprocess was used as a reference. The extraction process to obtain silica without bioprocess is the same described previously using calcination and acid treatment.

Silica powders were characterized to 64 scans by employing a Fourier transform infrared spectrophotometer (FTIR) Bruker Vector 33 with a resolution of 4 cm−1, using KBr powders. Raman spectroscopy was performed in a Raman Senterra Bruker machine with a 100x microscope objective, laser emitting, at 785 nm and resolution 0.1 cm−1. Transmission Electron Microscopy (TEM) was performed using a JEOL TEM-1010 transmission electron microscope. Average particle size was determined by Dynamic Light Scattering (DLS) using a Brookhaven model BI200SM with laser He-Ne of 35 mW model 9167 EB-1 Melles-Griot. Elemental analysis was carried out using energy dispersion spectroscopy (EDS) mean software Oxford Inca X-Sight. EDS is adapted in equipment JEOL JSM-6060 LV Scanning Electron Microscope. X-ray Diffraction (XRD) was performed in a diffractometer Rigaku, Model MiniFlex, with a wavelength from 1.54  corresponding to ka cupper radiations. Crystalline structures present in the samples were analysed with Materials Data Jade software of MDI Materials Data.

3. Results and Discussion

3.1. Infrared Spectroscopy (FT-IR)

Figure 1 presents FT-IR spectra of both samples of silica (with and without bioprocess). Every spectrum shows a wide peak at 3263 cm−1 ascribable to the O–H stretching mode of water molecules as well as a peak assigned to the water hydroxyl deformation vibration at 1630 cm−1—these bands correspond to adsorbed water that minerals contain physically [25, 26]. At 1379 cm−1, there exists a band associated with the mineral phases of carbonates (i.e., calcite, dolomite, and aragonite); these compounds are common in soils and are generally produced by a biomineralization process. Although the carbonates can be thermally unstable, their stability increases with the type of cation associated and so can prevail even in the treatment conditions of the sample [27]. This band is less intense in the sample with bioprocess due in great part to the fact that this mineral source can be necessary in the metabolism of the earthworms. A band corresponding to Si–O asymmetrical stretching vibration was localized at 1056 cm−1 [28], and this band is very similar in both samples with and without bioprocess. Another band localized at 797 cm−1 (Si–O) is related to the presence of quartz in the sample [29]. In the region between 400 and 600 cm−1, the sample with bioprocess shows a peak at 457 cm−1 corresponding to Si–O–Si bending vibration [30]; without bioprocess the sample exhibits a peak in 603 cm−1; this can be assigned to a compound silicate that contains magnesium [31]. In the bioprocess is a band not observed; however this can overlap with the band localized in 457 cm−1. The results of FTIR show the existence of bands where silica prevails, but the differences in these bands (with and without bioprocess) can aid in explaining the mechanism of the bioprocess in the earthworms.

3.2. Raman Spectroscopy

The FT-Raman spectrum of the sample with and without bioprocess is shown in Figures 2(a) and 2(b). FT-Raman bands were well defined only in the sample of silica with bioprocess (Figure 2(a)). These bands are localized at 122 cm−1, 210 cm−1, and 468 cm−1. The first band at 122 cm−1 corresponds to an O–Si–O symmetric bend; the second band localized at 210 cm−1 is assigned to stretch vibration modes of O–H group, while the intense band localized at 468 cm−1 is associated with the Si–O–Si stretching vibration. This last band has a stronger intensity and belongs to the polymorph of silica α-quartz typically found at 465 cm−1 [32]. FT-Raman results confirm the presence of silica and suggest that in samples with bioprocess a crystalline arrangement is present in contrast with the samples without bioprocess, thus confirming that microorganisms contribute to the molecular ordering.

3.3. Transmission Electron Microscopy (TEM)

TEM images of silica sample with bioprocess are shown in Figures 3(a)3(c). In this case, the particles extracted using the annelid bioprocess have a morphology similar to spherical, they are grouped in clusters, and have a nanometric size. TEM images of silica sample without bioprocess are shown in Figures 3(d)3(f). In this figure, particles were not identified nor had their morphology defined, but clusters and agglomerates were observed and their size apparently was bigger than particles without bioprocess. The results showed a difference in the morphology, dispersion, and size between the samples. Without the bioprocess, the particles have a tendency to be amorphous, while, with the bioprocess, these particles display more order and these differences are attributed to the vermicomposting bioprocess. Microorganisms play important role in this process due to the activity of classification and purification of the matter employed in their metabolic process.

3.4. X-Ray Diffraction (XRD)

XRD diffractograms of the sample of silica with the bioprocess are given in Figure 4(a). Figure 4(a) shows characteristic peaks related to hexagonal quartz (Figure 4(a), peak 1)—this quartz has been identified earlier as belonging to a polymorph of silica. Also hexagonal tridymite (primitive) (Figure 4(a), peak 2) and triclinic albite (Figure 4(a), peak 3) polymorphs were identified. XRD diffractograms of the sample without the bioprocess are given in Figure 4(b). Figure 4(b) shows that the particles have a structure essentially amorphous and only two peaks related to hexagonal quartz polymorphs can be detected slightly (Figure 4(b), peaks 1). These results confirm that the bioprocess plays an important role in the transformation of the particles toward a crystalline structure. In this type of grass, polymorphs of silicates prevail, although, as can be observed in EDS, mineral elements exist that can produce other crystalline structures.

3.5. Dynamic Light Scattering (DLS)

The mean diameter of particle estimated by DLS showed that with the bioprocess the particles achieved 530 nanometres while without the bioprocess the mean diameter was 1.6 micrometres. These results show that with the bioprocess the size of silica particles is smaller than the size of those without bioprocess. The mineral portion (phytoliths) in grass is generally microscopic; however, the metabolic activity of microorganisms inside the intestine of earthworms causes an important size reduction. This analysis shows that the size of particle can be affected by the trend of the samples to form agglomerates; this can be better observed in the sample without bioprocess.

3.6. Energy Dispersion Spectroscopy (EDS)

Table 1 summarizes the results obtained using energy dispersion spectroscopy. A significant amount of silicon and oxygen weight percentage was observed in the samples: with bioprocess: 54.01% O and 30.69% Si and without bioprocess: 56.23% O and 35.44% Si. Table 1 shows other elements in lower proportion related to the biomineralization process and some were detected using the technique of X-ray Diffraction (Figure 4). Elements such as magnesium, aluminium, and iron increased their proportion when the bioprocess is used. The relationship of oxygen and silicon in the samples is similar, although the oxygen is slightly lower in the sample with the bioprocess due to this element being an important source in the metabolic process of earthworms and microorganisms. EDS showed the mineral elements in the samples with and without the bioprocess, and it is important to remark that elements such as sodium and calcium only are shown in the sample without the bioprocess, while in the bioprocess are elements that are an important source in the nutritional process of earthworms and can be used by the microorganisms.

4. Conclusions

The effect produced by the annelid bioprocess on the properties of silica particles obtained from St. Augustine grass was determined. The characterization of these particles was performed with FTIR, Raman spectroscopy, TEM, XDR, DLS, and EDS. The particles obtained from the bioprocess contain mainly silica and OH groups and present a trend toward a spherical morphology; their size estimate by DLS was 530 nm, which is smaller than those particles without the bioprocess. The bioprocess produced structural order and crystalline particles with prevailing α-quartz phase and other silicates such as tridymite and albite. The bioprocess shows others elements in minor proportion such as aluminium, magnesium, iron, and potassium. The characteristics of these types of particles obtained from the bioprocess using vermicompost and grass can contribute to explaining of the biological mechanism of vermicomposting specifically referred to as biomineralization. The results showed changes between the samples with and without the bioprocess. These changes are produced in the digestion process of earthworms together with the microorganisms involving separation, classification, purification, and transformation of the matter and therefore are named as biotransformation. This biological mechanism represents a novel alternative to create novel materials in a cheap and ecofriendly biostructure based manner.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgments

The authors are grateful to Ms. Maria de Lourdes Palma for her assistance in TEM, to Dr. Genoveva Hernandez-Padron for her assistance in IR and Raman analysis, to Dr. Eric Rivera for his assistance in XRD, to Dr. Miriam Estevez Gonzalez for her assistance in DLS analysis, and also to M. T. Carrillo. Financial support from the National Council for Science and Technology of Mexico (CONACYT) (PhD Scholarship to A. Espíndola-Gonzalez) is gratefully acknowledged.