Influence of Styrene-Acrylic Ester Dispersion on the Early Hydration of Cement
Table 5
The integrated results of XRD peak of AFt in the pastes with SAE dispersion.
| Curing time | | | (counts·s−1) | (counts·s−1) | |
| 10 minutes | 0% | 9.696 | 374 | 2396 | 1.00 | 5% | 9.709 | 255 | 1623 | 0.72 | 10% | 9.668 | 311 | 1983 | 0.91 | 15% | 9.606 | 319 | 2041 | 0.98 | 20% | 9.704 | 222 | 1411 | 0.71 |
| 1 hour | 0% | 9.712 | 461 | 2783 | 1.00 | 5% | 9.675 | 618 | 3977 | 1.50 | 10% | 9.688 | 471 | 3023 | 1.19 | 15% | 9.623 | 374 | 2293 | 0.95 | 20% | 9.525 | 139 | 975 | 0.42 |
| 4 hours | 0% | 9.762 | 320 | 2043 | 1.00 | 5% | 9.671 | 473 | 3452 | 1.77 | 10% | 9.667 | 414 | 2654 | 1.42 | 15% | 9.723 | 276 | 1832 | 0.98 | 20% | 9.627 | 170 | 1072 | 0.64 |
| 6 hours | 0% | 9.692 | 495 | 3192 | 1.00 | 5% | 9.651 | 825 | 5320 | 1.75 | 10% | 9.565 | 374 | 3386 | 1.17 | 15% | 9.687 | 459 | 2672 | 0.96 | 20% | 9.629 | 194 | 1226 | 0.46 |
| 8 hours | 0% | 9.795 | 596 | 3882 | 1.00 | 5% | 9.71 | 742 | 4783 | 1.29 | 10% | 9.688 | 509 | 4362 | 1.24 | 15% | 9.647 | 321 | 2527 | 0.60 | 20% | 9.585 | 167 | 1151 | 0.36 |
| 12 hours | 0% | 9.711 | 814 | 4073 | 1.00 | 5% | 9.669 | 1091 | 7050 | 1.82 | 10% | 9.709 | 672 | 6032 | 1.63 | 15% | 9.626 | 533 | 3426 | 0.97 | 20% | 9.647 | 301 | 1921 | 0.57 |
| 1 day | 0% | 9.711 | 649 | 3967 | 1.00 | 5% | 9.711 | 783 | 6183 | 1.64 | 10% | 9.688 | 714 | 5971 | 1.66 | 15% | 9.667 | 660 | 5523 | 1.60 | 20% | 9.646 | 342 | 2186 | 0.66 |
| 3 days | 0% | 9.731 | 572 | 3594 | 1.00 | 5% | 9.667 | 1048 | 6772 | 1.98 | 10% | 9.731 | 1064 | 6439 | 1.97 | 15% | 9.646 | 960 | 6202 | 1.98 | 20% | 9.625 | 586 | 3766 | 1.26 |
|
|
: interplanar spacing; , : intensities of XRD pattern for maximum and integrate; = (1 + )/().
|