A Precipitation Phenomenon of Titanium Compounds in Aluminum Melts and the Refinement Fading Mechanism of the Al-5Ti-0.62C Master Alloy
Figure 6
SEM images of the precipitation layers at the bottom of the samples of remelted Al-5Ti-0.62C master alloy after 180 min of heat treatment: (a) 180 min, SEM image; (b) SEM image of aggregated particles at the α-Al grain boundary.