Advances in Materials Science and Engineering / 2015 / Article / Tab 4 / Research Article
Modeling and Analysis of Mechanical Properties of Aluminium Alloy (A413) Processed through Squeeze Casting Route Using Artificial Neural Network Model and Statistical Technique Table 4 Assigned orthogonal L27 with the acquired data.
S. number Squeeze pressure (MPa) Die preheating temperature (°C) Melt temperature (°C) Hardness (BHN) UTS (MPa) YS (MPa) 1 70 150 650 72 252 149 2 70 225 650 76 266 147 3 70 300 650 65 236 136 4 70 150 725 71 249 146 5 70 225 725 78 269 152 6 70 300 725 66 237 135 7 70 150 800 72 239 135 8 70 225 800 75 248 141 9 70 300 800 62 232 131 10 105 150 650 84 285 158 11 105 225 650 87 289 167 12 105 300 650 79 258 142 13 105 150 725 89 284 166 14 105 225 725 88 293 167 15 105 300 725 81 274 158 16 105 150 800 78 265 156 17 105 225 800 87 291 161 18 105 300 800 79 258 149 19 140 150 650 94 298 171 20 140 225 650 92 299 174 21 140 300 650 87 286 162 22 140 150 725 94 301 167 23 140 225 725 95 305 176 24 140 300 725 87 287 169 25 140 150 800 91 285 166 26 140 225 800 92 299 171 27 140 300 800 83 284 162