Preparation and Properties of OMMT/PU Composites
Table 1
Tensile strength and elongation at failure of OMMT/PU.
| Index sample | Thickness (mm) | Width (mm) | Gauge length (mm) | Tensile force (MPa) | Elongation at break (%) | Tensile strength at break (MPa) |
| Pure | 1.883 | 6.103 | 30.10 | 13.89 | 20.4 | 1.21 | I | 1.786 | 6.385 | 32.94 | 15.87 | 31.76 | 1.391 | II | 1.863 | 6.075 | 33.61 | 16.64 | 34.44 | 1.471 | III | 2.012 | 6.207 | 37.45 | 22.02 | 49.80 | 1.761 | IV | 2.113 | 6.015 | 36.98 | 27.16 | 47.92 | 2.14 | V | 1.996 | 6.154 | 36.27 | 18.44 | 45.08 | 1.50 |
|
|