The Effect of Welding Residual Stress for Making Artificial Stress Corrosion Crack in the STS 304 Pipe

<table class="table-group" id="tab2"><tr><td><table class="table"><tr><td class="thead-hr" colspan="2"><hr/></td></tr><tr><td align="left">Welding current (A)</td><td align="center">90</td></tr><tr><td align="left">Welding voltage (V)</td><td align="center">21</td></tr><tr><td align="left">Welding speed (cm/min)</td><td align="center">30</td></tr><tr><td align="left">Shielding gas</td><td align="center">Ar 100%</td></tr><tr class="table-tr"><td colspan="2"><hr class="tbody-hr"/></td></tr></table></td></tr></table>

Advances in Materials Science and Engineering

tab2

Table 2

Table 2: The Effect of Welding Residual Stress for Making Artificial Stress Corrosion Crack in the STS 304 Pipe 