Research Article
Effects of Static Magnetic Fields on the Physical, Mechanical, and Microstructural Properties of Cement Pastes
Table 1
Chemical composition and physical and mechanical properties of the cement used.
| Chemical analysis | Specification | Result | NMX-C-414-ONNCCE |
| SiO2 | — | 22.97 |
Al2O3 | — | 4.53 | Fe2O3 | — | 2.72 | CaOt | — | 61.38 | CaOL | — | 0.47 | MgO | — | 1.46 | SO3 | 4.0% max. | 2.61 | R.I. | — | 8.14 | Na2O | — | 0.65 | K2O | — | 1.10 | Blaine (cm2/g) | — | 4327 | % Fineness sieve size 325 (45 μm) | — | 1.60 | Sanity | | | Expansion | 0.80% max. | — | Shrinkage | 0.20% max. | −0.03 | Time of setting by Vicat needle (min) | | | Initial | 45 min. | 192 | Final | 375 max. | 313 | False set% | — | 79 | Compressive strength (N/mm2) | | | 1 day | — | 16.9 | 3 days | 20 min. | 28.8 | 7 days | — | 34.9 | 28 days | 30–50 | 40.8 |
|
|