Industrial versus Laboratory Clinker Processing Using Grinding Aids (Scale Effect)
Table 5
Ec and cement properties following laboratory grinding.
| | Control cement |
Cement with glycol-based GA at 530 g/ton |
Cement with amine-based GA at 460 g/ton | Test number | 1 | 2 | 1 | 2 | 1 | 2 |
| Ec, kWh/ton | 43.27 | 43.27 | 39.6 | 38.87 | 40.33 | 40.33 | 43.27 (0%) | 39.23 (1.31%) | 40.33 (0%) |
| Blaine, cm2/g | 3870 | 3825 | 3810 | 3775 | 3880 | 3790 | 3848 (0.82%) | 3792 (0.65%) | 3835 (1.66%) |
| R-90, % | 5.8 | 5.3 | 6.7 | 7.4 | 5.7 | 6.4 | 5.55 (6.37%) | 7.05 (7.02%) | 6.05 (8.2%) |
| R-45, % | 18.3 | 17.7 | 23 | 23.3 | 19.6 | 22 | 18 (2.36%) | 23.15 (0.91%) | 20.8 (8.16%) |
| | 0.893 | 0.888 | 0.782 | 0.81 | 0.748 | 0.771 | 0.891 (0.39%) | 0.796 (2.48%) | 0.759 (2.14%) |
| , m | 23.5 | 25.1 | 27.8 | 26.92 | 29 | 25.8 | 24.3 (4.65%) | 27.35 (2.32%) | 27.4 (8.26%) |
| Water demand, % | 27.7 | 27.8 | 27.9 | 27.5 | 27.7 | 27.3 | 27.75 (0.25%) | 27.7 (1.02%) | 27.5 (1.03%) |
| Final setting, min | 210 | 215 | 225 | 215 | 205 | 190 | 212.5 (1.7%) | 220 (3.21%) | 197.5 (5.37%) |
| 1-day compression, MPa | 14.3 | 14.7 | 16.3 | 15.9 | 17 | 15.8 | 14.5 (1.95%) | 16.1 (1.75%) | 16.4 (5.17%) |
| 28-day compression, MPa | 46.4 | 44.8 | 42 | 44.2 | 54.3 | 49.2 | 45.6 (2.48%) | 43.1 (3.61%) | 51.7 (6.97%) |
|
|
The mean of two values is considered for analysis. The COV is given between parentheses.
|