Characterization of Waste Material Derived Willemite-Based Glass-Ceramics Doped with Erbium
Figure 4
Grain size distribution of 3 wt% Er3+ doped willemite-based glass-ceramic crystals in the glass-ceramic samples sintered at 900°C for 4 h.