Numerical and Experimental Investigation on the Structural Behaviour of a Horizontal Stabilizer under Critical Aerodynamic Loading Conditions
Table 2
Mechanical material properties of lamina HTA 5131/RTM6.
| Longitudinal Young Modulus, | 92.10 GPa | Transverse Young Modulus, | 7.61 GPa | In Plane Shear Modulus, | 3.26 GPa | In Plane Shear Modulus, | 3.26 GPa | Poisson ratio, | 0.36 | Poisson ratio, | 0.48 | Longitudinal tensile strength | 1222 MPa | Longitudinal compressive strength | 654 MPa | Transverse tensile strength | 42.8 MPa | Transverse compressive strength | 104 MPa | Shear strength | 62.5 MPa | Ply thickness | 0.28 mm |
|
|