Nanohydroxyapatite Silicate-Based Cement Improves the Primary Stability of Dental Implants: An In Vitro Study

Khorshidi, Hooman; Raoofi, Saeed; Najafi, Maryam; Kalantari, Mohammad Hassan; Khorshidi Malahmadi, Jamshid; Derafshi, Reza

doi:https://doi.org/10.1155/2017/2306025

Advances in Materials Science and Engineering

On this page

Abstract Introduction Materials and Methods Results and Discussion Conclusions Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2017 | Article ID 2306025 | https://doi.org/10.1155/2017/2306025

Nanohydroxyapatite Silicate-Based Cement Improves the Primary Stability of Dental Implants: An In Vitro Study

Hooman Khorshidi,¹Saeed Raoofi,¹Maryam Najafi,¹Mohammad Hassan Kalantari,²Jamshid Khorshidi Malahmadi,³and Reza Derafshi²

Academic Editor: Michele Iafisco

Received03 Nov 2016

Revised15 Dec 2016

Accepted15 Jan 2017

Published19 Feb 2017

Abstract

Objectives. Insufficient cortical bone volume when placing implants can lead to lack of primary stability. The use of cement as a bone fill material in bone defects around dental implant could result in better clinical outcome. HA has shown excellent biological properties in implant dentistry. The purpose of this study was to evaluate the effect of nanohydroxyapatite powder (Nano-HA) in combination with accelerated Portland cement (APC) on implant primary stability in surgically created circumferential bone defects in a bovine rib in vitro model. Materials and Methods. Sixteen bovine rib bones and thirty-six implants of same type and size (4 mm × 10 mm) were used. Implants were divided into six groups: no circumferential bone defect, defect and no grafting, bone chips grafting, Nano-HA grafting, APC grafting, and Nano-HA mixed to APC grafting (Nano-HA-APC). Circumferential defects around the implants were prepared. The implant stability quotient (ISQ) values were measured before and after the grafting. Results. APC exhibited the highest ISQ values. A significant increase of ISQ values following the grafting of Nano-HA-APC () and APC alone () was achieved. Increase of ISQ values after 72 hours was and , respectively. Nano-HA grafting alone exhibited the least rise in ISQ values. Conclusions. Nanohydroxyapatite silicate-based cement could improve the primary stability of dental implants in circumferential bone defect around implants.

1. Introduction

Primary stability is defined as the degree of the mechanical anchoring established when placing an implant. High primary stability is critical for a successful osseointegration of dental implants [1]. A safe primary stability is positively attendant with a secondary stability (osseointegration) [2]. Weakened primary implant stability has been demonstrated to threaten the osseointegration process [3]. Several variations in surgical technique have been described to assist in enhancing primary stability of dental implants, in order to increase the success rate of dental implants and to reduce the overall treatment duration [1, 4, 5]. Insufficient cortical bone volume when placing implants can lead to lack of primary stability. Using a bone graft material around the arranged implant beds was also suggested as a technique to overcome insufficient primary stability of the dental implant [6]. Some materials were assessed for this purpose and they demonstrated encouraging results [6, 7]. Calcium-silicate cements, like MTA (mineral trioxide aggregate) and other Portland-derived materials, are hydraulic cements mainly composed of tricalcium and dicalcium silicate, tricalcium aluminate, and calcium sulphate. A longlist of new materials based on the original Portland cement formulation and/or with minor modifications has been introduced in dental practice [8]. The setting time of Portland cement can be decreased by adding calcium chloride (CaCl₂), known as accelerated Portland cement (APC) [9]. Nevertheless, a generic name for this class of materials, Hydraulic Silicate Cement (HSC), has been proposed [10]. It has been suggested that HSC materials can possess the properties to nucleate apatite and may play a positive role as a cell differentiation promoter and also for stimulating tissue repair, osteogenesis, and cementogenesis [8]. In a study on “Kinetics of apatite formation in SBF of a HCSC Portland-based cement monitored over time by SEM and EDX analyses,” it has been reported that after 7-day soaking in SBF the surface became covered by aggregated spherulites and consequently with long (28 days) soaking times the cement surface shifted from a calcium silicate to a calcium phosphate composition [8]. Kinetic reaction is directly affected by the high surface area of nanoparticles. A number of calcium phosphates (including hydroxyapatite) were introduced in experimental HCS to serve as a reservoir of phosphate and apatite deposits [8, 11]. APC has the advantage of good handling and manipulation compared other HSC [9, 12]. Easy handling of bone substitutes in implant dentistry is crucial. For many clinical applications, the main limitation of HA granules in implant surgery was the difficult handling. Nevertheless, hydroxyapatite is a well-known bone substitute [13]. Hydroxyapatite shows excellent biocompatibility with soft tissues, making it an ideal candidate for dental implants [14]. However, it is not expected that excellent biological properties of HA can increase the early fixation of implants. Early fixation (or in other words primary stability) understood as the mechanical anchoring right after placing an implant. Recently, considerable researches have been carried out on the nanohydroxyapatite [15–18]. HA particles with nanometer sizes (<100 nm) are favorable for use as implant donor substances, because they simulate the nanostructure of the inorganic phase in natural bones [15]. On the other hand, HA nanoparticles were found to provide a high surface area per HA volume, resulting in increased cellular adherence, proliferation, and osteoblast adhesion [15, 18]. Therefore, the aim of this study was to evaluate the effect of nanohydroxyapatite powder (Nano-HA) in combination with APC on implant primary stability in surgically created circumferential bone defects in a bovine rib in vitro model.

2. Materials and Methods

Sixteen frozen bovine rib bones from an Iranian bull or cow were utilized in this study. The rib bones were left at room temperature for 2 h; they were stabilized for the drilling procedure, grafting, and measurements, and their periosteum was removed before drilling. 36 dental implants with an 11° Morse taper, internal connection-type, and with a self-tapping fixture design were used (KME Co, Iran). All implants have the same size .

A pilot study was conducted to determine the depth of defect that affects the primary stability of the implant. The drilling sequence was performed according to the manufacturer’s instructions and implant beds were prepared for an implant of 3.5 mm in diameter and 10 mm in length. Subsequently, circumferential cortical bone defects were prepared by perforating a defect with a diameter of 6.5 mm. The depth of the defect gradually was increased and the ISQ value measured. By the depth of 3 mm, a sudden reduction in the ISQ value (decrease of 15–25 units) was observed; thus, it was decided to create a circumferential defect by the depth of 3 mm and a diameter of 6.5 mm around each implant. Moreover, the cross-section of the rib was prepared to find the appropriate portion with the best volume and density of the available bone. It was decided to use the beginning part of dorsal surface of all ribs (near the head of the rib that is connected to the spinal cord), in this experiment (Figure 1).

In each rib bone, 2-3 implant beds were prepared in the mentioned area, and the centers of the implant beds were 40 mm apart. There was 6 groups in the experiment: (1) positive control group: no defect, (2) negative control group: defect and no grafting, (3) defect and bone chips grafting, (4) defect and Nano-HA grafting, (5) defect and APC grafting, and (6) defect and Nano-HA-APC grafting. For each group, 6 implants were utilized. The drilling sequence was performed according to the manufacturer’s instruction and implant beds were prepared by 3.5 mm diameter and 10 mm length. Subsequently, for creating the circumferential defect around implant, drilling continued with a shorter 8 mm drill with 6.5 mm diameter. Thus, after installation of implant there was 1.5 mm circumferential defect around the implant with 8 mm depth (Figure 2).

Bone chips were collected during drilling. However, it was an autogenous bone and thus do not require any further preparation. Nano-Ha (Pardis Pajoohesh Fanavaran Yazd, Yazd Science and Technology Park, Yazd, Iran) did not require any preparation as well.

To prepare APC, 10% vol calcium chloride (Kimia Material Co, Iran) was added to 90% vol of Portland cement type 1 (Fars Cement Co, Iran). Since manipulation and handling of the material is a matter of major importance, therefore several combinations of HA and APC by volume were evaluated and the mixture of 75% vol of Nano-HA and 25% vol of APC was elected. In addition a pilot study was done for evaluating the material and the specimens were fabricated according to standards for the compressive and tensile strength test by test machine Zwick/Roell Z020. The APC and Nano-HA-APC cements were placed in cylindrical molds with 15 mm length and 10 mm in diameter. They were stored at room temperature for 48 h, and then the samples were removed from the mold. The compressive and tensile strength tests were performed in test machine with 1 N preload, at 0.1 mm/minute speed. The maximum stress was recorded in MPa, using the maximum compressive and tensile force as well as the diameter of the cylinders (MPa = N/mm²). Compressive and tensile strength of APC were measured as 1.18 (one tested specimen) and 0.72 MPa (one tested specimen). Compressive and tensile strength of Nano-HA-APC were measured as 1.27 (one tested specimen) and 0.54 MPa (two tested specimens, SD: 0.18 MPa). Considering that only one or two samples were tested in this pilot study, it is difficult to conclude that mixing APC with Nano-HA would increase compressive strength and/or reduce tensile strength compared to APC.

2.1. Implant Insertion, Grafting, and ISQ Measurement

Resonance Frequency Analysis (RFA) measures the frequency with which a device vibrates. The stability of a dental implant can be determined as the resonance frequency changes with different stabilities. The implant stability quotient (ISQ) is a global standard for measuring implant stability as measured by RFA. ISQ scale ranges from 1 to 100, but the acceptable stability range lies between 55 and 85. Implants were placed in each prepared hole and ISQ values were measured four times from the four perpendicular directions with an Osstell instrument and smart peg no. 47. APC was mixed with water at a 2 : 1 ratio [9, 12]; Nano-HA-APC was mixed with water at a 3 : 1 ratio (with consult by a biomaterial master) [19]. Graft materials were inserted into defect by a spatula. ISQ values were measured four times from the four perpendicular same directions again. APC and Nano-HA-APC were allowed to harden for 20 min before second measurement. Lastly, the ISQ values will be measured again after 72 h, after APC and Nano-HA-APC grafting, because these two materials had setting (Figure 3).

ISQ value was measured in four directions for each implant before and after grafting and then compared ISQ value changes before and after grafting in the same direction and same implant. ISQ values were measured before grafting (ISQ 1), after grafting (ISQ 2), and after 72 h (ISQ 3) in the same directions and same implant.

2.2. Statistical Analysis

All quantitative data were expressed as the mean and standard deviation. Statistical analysis was performed through Kolmogorov-Smirnov -test, nonparametric Kruskal-Wallis, Mann–Whitney U tests, and Wilcoxon test using SPSS version 22 (SPSS Ltd., Hong Kong). A value of was considered statistically significant.

3. Results and Discussion

ISQ value for bone without any defect was measured by four different directions in 6 implants. The maximum ISQ value was 76 and the minimum ISQ value was 68. The mean ISQ value for intact bone was 72.25. The changes in ISQ value before and after the application of each graft are shown in Table 1.

The mean increase of ISQ values after grafting was statistically significant for every grafting material except for Nano-HA grafting group ( for APC and Nano-HA-APC, for bone chips, for Nano-HA).

While increase in ISQ values after APC grafting was compared with Nano-HA-APC grafting, the increase in ISQ values was not significant (). The ISQ improvement in APC and Nano-HA-APC groups in the first 24 hrs was 18.08 and 9.5, respectively. But increasing of ISQ value in the period of 24–72 hrs was dissimilar in the groups. (The difference between ISQ 2 and ISQ 3 was 6 for APC and 8 for Nano-HA-APC.) It seems that this difference would be related to incorporation of nanoparticles in the Nano-HA-APC cement.

In this study, the application of Nano-HA in combination with APC (Nano-HA-APC) around dental implants with insufficient primary stability was assessed as bone cement grafting. This study was not intended to explore Nano-HA instead of APC. The object of this study was to explore the potential mechanical advantages of APC when added to the Nano-HA as a bone graft substitute in clinical implant surgeries. One of these clinical implications would be providing the primary implant stability in circumferential bone defects around the implants. Results of the current study indicated a significant improvement in primary stability following the grafting of APC, Nano-HA-APC, and bone chips in all implants compared to Nano-HA (Figure 4).

This improvement of primary stability was greater by grafting APC and Nano-HA-APC. By grafting of APC, improvement similar to intact bone and even superior to intact bone was achieved. On the other hand, the increase of primary stability by bone chips was not as much as APC and Nano-HA-APC. Nano-HA grafting did not affect the low primary stability. These results are in line with the results obtained by Poly bone [6, 20] and Dental Implant Bone Cement [21].

The aim of the study was to evaluate the effect of selected materials on implant initial stability However, the measurement is performed on the third day for silicate-based materials. APC generally exhibited the highest ISQ values. Although results of ISQ value improvement in APC group statistically were better than HA_APC group, but from the clinically point of view both results are acceptable and in another word the result is the same. ISQ scale ranges from 1 to 100, but the acceptable stability range lies between 55 and 85 ISQ. The ISQ 3 (72 hours after grafting) value results for APC-Nano-HA were in acceptable range. But the Nano-HA alone could not obtain acceptable ISQ value in this study. The proposed combination of APC and Nano-HA was able to make an acceptable primary stability in circumferential bone defect around dental implant (Figure 5). In our preliminary experiment, the compressive strength of Nano-HA-APC was higher than APC (1.18 versus 1.27 MPa) but, in primary stability test, ISQ value of APC was higher than Nano-HA-APC group. Accordingly the compressive strength of the material cannot necessarily predict the improvement in ISQ values as well as the primary stability of implant in circumferential bone defects.

4. Conclusions

Nanohydroxyapatite powder alone could not enhance the primary stability of dental implants in the circumferential bone defects.

Silicate-based cement alone may well improve the primary stability of dental implants in the circumferential bone defects to an ISQ value, similar to an ISQ value of direct contact of implant to bone preparation sites.

Nanohydroxyapatite silicate-based cement 9 Nano-HA 75% vol and APC 25% vol could improve the primary stability of dental implants in circumferential bone defect around implants to an acceptable stability range of ISQ value.

Competing Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgments

The authors appreciate the funding and support for this study provided by the Vice Chancellor of Research Center & Innovation, Shiraz University of Medical Sciences. The authors wish to thank Dr. Mehrdad Vosoughi of the Dental School of Shiraz University of Medical Sciences for assistance with the statistical analysis.

References

M. Ketabi, D. Deporter, and E. G. Atenafu, “A systematic review of outcomes following immediate molar implant placement based on recently published studies,” Clinical Implant Dentistry and Related Research, vol. 18, no. 6, pp. 1084–1094, 2016.
View at: Publisher Site | Google Scholar
F. Javed and G. E. Romanos, “The role of primary stability for successful immediate loading of dental implants. A literature review,” Journal of Dentistry, vol. 38, no. 8, pp. 612–620, 2010.
View at: Publisher Site | Google Scholar
R. Wang, S. J. Eppell, C. Nguyen, and N. Morris, “Relative contribution of trabecular and cortical bone to primary implant stability: an in vitro model study,” Journal of Oral Implantology, vol. 42, no. 2, pp. 145–152, 2016.
View at: Publisher Site | Google Scholar
S. A. Gehrke, J. L. C. Guirado, R. Bettach, M. D. Fabbro, C. P.-A. Martínez, and J. A. Shibli, “Evaluation of the insertion torque, implant stability quotient and drilled hole quality for different drill design: an in vitro investigation,” Clinical Oral Implants Research, 2016.
View at: Publisher Site | Google Scholar
S. A. Gandhi, J. A. Baker, L. Bairam, H.-I. Kim, E. L. Davis, and S. Andreana, “Primary stability comparison using piezoelectric or conventional implant site preparation systems in cancellous bone: a pilot study,” Implant Dentistry, vol. 23, no. 1, pp. 79–84, 2014.
View at: Publisher Site | Google Scholar
S.-Y. Shin, S.-I. Shin, S.-B. Kye et al., “Bone cement grafting increases implant primary stability in circumferential cortical bone defects,” Journal of Periodontal & Implant Science, vol. 45, no. 1, pp. 30–35, 2015.
View at: Publisher Site | Google Scholar
N. F. Oliscovicz, A. C. Shimano, É. Jr. Marcantonio, C. P. Lepri, and A. C. Dos Reis, “Analysis of primary stability of dental implants inserted in different substrates using the pullout test and insertion torque,” International Journal of Dentistry, vol. 2013, Article ID 194987, 5 pages, 2013.
View at: Publisher Site | Google Scholar
C. Prati and M. G. Gandolfi, “Calcium silicate bioactive cements: biological perspectives and clinical applications,” Dental Materials, vol. 31, no. 4, pp. 351–370, 2015.
View at: Publisher Site | Google Scholar
S. Dokami, S. Raoofi, M. J. Ashraf, and H. Khorshidi, “Histological analysis of the effect of accelerated portland cement as a bone graft substitute on experimentally-created three-walled intrabony defects in dogs,” Journal of Dental Research, Dental Clinics, Dental Prospects, vol. 1, no. 3, pp. 131–135, 2007.
View at: Google Scholar
B. W. Darvell and R. C. T. Wu, “MTA—an hydraulic silicate cement: review update and setting reaction,” Dental Materials, vol. 27, no. 5, pp. 407–422, 2011.
View at: Publisher Site | Google Scholar
M. G. Gandolfi, G. Ciapetti, P. Taddei et al., “Apatite formation on bioactive calcium-silicate cements for dentistry affects surface topography and human marrow stromal cells proliferation,” Dental Materials, vol. 26, no. 10, pp. 974–992, 2010.
View at: Publisher Site | Google Scholar
H. Khorshidi, S. Raoofi, S. Sabagh, Z. Behboud, G. Mozafari, and M. J. Ashraf, “Effect of combined calcium hydroxide and accelerated portland cement on bone formation and soft tissue healing in dog bone lesions,” Journal of Dental Biomaterials, vol. 2, no. 3, pp. 97–102, 2015.
View at: Google Scholar
S. R. Dutta, D. Passi, P. Singh, and A. Bhuibhar, “Ceramic and non-ceramic hydroxyapatite as a bone graft material: a brief review,” Irish Journal of Medical Science, vol. 184, no. 1, pp. 101–106, 2015.
View at: Publisher Site | Google Scholar
H. Zhou and J. Lee, “Nanoscale hydroxyapatite particles for bone tissue engineering,” Acta Biomaterialia, vol. 7, no. 7, pp. 2769–2781, 2011.
View at: Publisher Site | Google Scholar
J. Venkatesan and S.-K. Kim, “Nano-hydroxyapatite composite biomaterials for bone tissue engineering—a review,” Journal of Biomedical Nanotechnology, vol. 10, no. 10, pp. 3124–3140, 2014.
View at: Publisher Site | Google Scholar
E. Pepla, “Nano-hydroxyapatite and its applications in preventive, restorative and regenerative dentistry: a review of literature,” Annali di Stomatologia, vol. 5, no. 3, pp. 108–114, 2014.
View at: Publisher Site | Google Scholar
M. Zhao, H. Li, X. Liu et al., “Response of human osteoblast to n-HA/PEEK—quantitative proteomic study of bio-effects of nano-hydroxyapatite composite,” Scientific Reports, vol. 6, Article ID 22832, 2016.
View at: Publisher Site | Google Scholar
S. M. Zakaria, S. H. S. Zein, M. R. Othman, F. Yang, and J. A. Jansen, “Nanophase hydroxyapatite as a biomaterial in advanced hard tissue engineering: a review,” Tissue Engineering—Part B: Reviews, vol. 19, no. 5, pp. 431–441, 2013.
View at: Publisher Site | Google Scholar
X. Wang, H. Xing, G. Zhang et al., “Restoration of a critical mandibular bone defect using human alveolar bone-derived stem cells and porous nano-HA/collagen/PLA scaffold,” Stem Cells International, vol. 2016, Article ID 8741641, 13 pages, 2016.
View at: Publisher Site | Google Scholar
B. M. Sehlke, T. G. Wilson, A. A. Jones, M. Yamashita, and D. L. Cochran, “The use of a magnesium-based bone cement to secure immediate dental implants,” The International journal of oral & maxillofacial implants, vol. 28, no. 6, pp. e357–e367, 2013.
View at: Publisher Site | Google Scholar
W.-J. Seong, S. Grami, S. C. Jeong, H. J. Conrad, and J. S. Hodges, “Comparison of push-in versus pull-out tests on bone-implant interfaces of rabbit tibia dental implant healing model,” Clinical Implant Dentistry and Related Research, vol. 15, no. 3, pp. 460–469, 2013.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2017 Hooman Khorshidi et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

1547

Downloads

1105

Citations