Study on Mechanical Relaxations of 7075 (Al–Zn–Mg) and 2024 (Al–Cu–Mg) Alloys by Application of the Time-Temperature Superposition Principle
Table 2
Chemical compositions of the as-received, commercial aluminum alloys (AA) 7075-T6 and 2024-T3.
| Aluminum alloy | Units | Si | Fe | Cu | Mn | Mg | Zn | Ti | Cr | Al |
| AA 7075-T6 | wt.% | 0.06 | 0.15 | 1.50 | 0.01 | 2.58 | 6.00 | 0.05 | 0.19 | 89.46 | at.% | 0.06 | 0.08 | 0.67 | 0.01 | 2.99 | 2.59 | 0.03 | 0.10 | 93.48 | AA 2024-T3 | wt.% | 0.18 | 0.28 | 4.46 | 0.64 | 1.35 | 0.04 | 0.05 | 0.01 | 92.98 | at.% | 0.18 | 0.14 | 1.95 | 0.32 | 1.54 | 0.02 | 0.03 | 0.01 | 95.81 |
|
|