Optimization of Alumina Slurry for Oxide-Oxide Ceramic Composites Manufactured by Injection Molding
Figure 8
Loss modulus versus frequency for B33 slurries containing varied PVA content from 0 to 16.48 wt%. Two tests illustrated T1 and T2.