Preparation, Characterization, and Evaluation of Humidity-Dependent Electrical Properties of Undoped and Niobium Oxide-Doped TiO2 : WO3 Mixed Powders
Table 3
Fit parameters for presented Nyquist plots of the sensor TiW-Nb4 at 20°C.
| RH (%) | R1 (Ω) | C1 (F) | R2 (Ω) | C2 (F) | R3 (Ω) | C3 (F) | Cgeo (F) | Ael (Ω−1) | nel | Apo (Ω−1) | npo | Asup (Ω−1) | nsup | Rsup (Ω) |
| 10 | 2.4E + 6 | 3.1E − 10 | 4.52E + 6 | 1.1E − 11 | 7.9E + 4 | 6.0E − 11 | 2.0E − 11 | 2.22E − 9 | 5.45E − 1 | 6.4E − 9 | 6.2E − 1 | 9.0E − 12 | 9.9E − 1 | 9.0E + 5 | 20 | 2.0E + 6 | 3.1E − 10 | 4.08E + 6 | 1.1E − 11 | 7.9E + 4 | 6.0E − 11 | 2.0E − 11 | 2.22E − 9 | 5.45E − 1 | 6.4E − 9 | 6.2E − 1 | 9.0E − 12 | 9.9E − 1 | 8.0E + 5 | 30 | 9.9E + 5 | 3.1E − 10 | 2.35E + 6 | 1.0E − 11 | 6.9E + 4 | 6.0E − 11 | 1.0E − 11 | 2.22E − 9 | 5.4E − 1 | 6.4E − 9 | 6.2E − 1 | 9.0E − 12 | 9.9E − 1 | 4.1E + 5 | 40 | 9.2E + 5 | 2.7E − 10 | 1.8E + 6 | 9.0E − 12 | 6.9E + 4 | 6.0E − 11 | 1.0E − 11 | 2.22E − 9 | 5.4E − 1 | 6.4E − 9 | 6.2E − 1 | 9.0E − 12 | 9.9E − 1 | 3.1E + 5 | 50 | 7.4E + 5 | 2.5E − 10 | 1.25E + 6 | 9.0E − 12 | 4.1E + 4 | 6.0E − 11 | 1.0E − 11 | 2.22E − 9 | 5.4E − 1 | 6.4E − 9 | 6.2E − 1 | 9.0E − 12 | 9.9E − 1 | 9.0E + 4 | 60 | 5.9E + 5 | 2.25E − 10 | 8.47E + 5 | 9.0E − 12 | 4.8E + 4 | 8.0E − 10 | 1.0E − 11 | 2.4E − 9 | 5.4E − 1 | 6.4E − 9 | 6.2E − 1 | 9.0E − 12 | 9.9E − 1 | 2.7E + 4 | 70 | 4.3E + 5 | 2.2E − 10 | 5.8E + 5 | 8.0E − 12 | 1.2E + 5 | 2.7E − 10 | 9.0E − 12 | 2.4E − 9 | 5.4E − 1 | 6.4E − 9 | 6.2E − 1 | 9.0E − 12 | 9.9E − 1 | 1.4E + 4 | 80 | 1.4E + 5 | 2.4E − 10 | 3.75E + 5 | 7.4E − 12 | 2.09E + 5 | 6.8E − 10 | 1.0E − 11 | 4.0E − 9 | 5.4E − 1 | 2.8E − 9 | 6.1E − 1 | 5.0E − 10 | 8.0E − 1 | 3.04E + 5 | 90 | 1.4E + 5 | 1.5E − 10 | 3.0E + 5 | 7.2E − 12 | 1.55E + 5 | 5.6E − 10 | 7.0E − 12 | 4.0E − 9 | 5.4E − 1 | 2.9E − 9 | 6.1E − 1 | 6.0E − 10 | 8.8E − 1 | 1.5E + 5 | 100 | 9.5E + 4 | 1.5E − 10 | 2.2E + 5 | 7.2E − 12 | 1.1E + 5 | 5.0E − 10 | 7.0E − 12 | 5.0E − 9 | 5.4E − 1 | 2.9E − 9 | 6.1E − 1 | 6.5E − 10 | 8.8E − 1 | 1.04E + 5 |
|
|