Effect of Reduction in Thickness and Rolling Conditions on Mechanical Properties and Microstructure of Rolled Mg-8Al-1Zn-1Ca Alloy

Table 3

Variation in the rolling conditions for samples 6–3 mm in thickness. The mechanical properties and mean grain size of the 6 mm thick alloy are provided.

Case	Roll temp.; (°C)	Sample temp.; (°C)	Rolling speed; (m/min)	mm; sample properties
The multipass rolling process	250	350	10	µm; YS 281 MPa; UTS 312 MPa; E1 6.6%
1	250	250
2	250	430
3	80	250
4	80	430