Research Article
Correlation of Process Parameters with Mechanical Properties of Laser Sintered PA12 Parts
Table 2
Comparison of maximum obtained values of present work with literature.
| | | Applied values | TS [MPa] | E-modulus [MPa] | EaB [%] | Density [g/cm3] | 0° | 90° | 0° | 90° | 0° | 90° | 0° | 90° |
| Present work | PA2200, EOS system | 0.26–0.86 J/mm3 | 50.1 | 51.2 | 2239 | 2171 | 25.9 | 15.6 | 0.953 | 0.951 | Caulfield et al. [2] | DuraForm PA, DTM Sinterstation | 0.19–0.36 J/mm3 | 48 | 44 | 1100 | 900 | 18 | 15 | 1.05 | 0.95 | Wegner and Witt [4] | PA2200, DTM Sinterstation | 0.23–0.67 J/mm3 | 51.3 | 48.9 | 1758 | 1692 | 21.1 | 13.7 | 0.998 | — | Negi et al. [5] | Glass filled PA, EOS system | 0.23–0.71 J/mm3 | 39.1 | — | 2460 | — | 16.4 | — | — | — |
|
|