Combustion and Mechanical Properties of Polymer-Modified Cement Mortar at High Temperature
Table 1
Physical properties of polymers.
| Type of polymer | Volatile portion (%) | Particle diameter (%) | Acid value (mgKOH/mg) | Apparent density (g/mL) |
| EVA | Less than 2.0 | Less than 2.0 | Less than 2.0 | 0.50 ± 0.10 | VVA | Less than 2.0 | Less than 2.0 | Less than 2.0 | 0.53 ± 0.10 | PAE | Less than 2.0 | Less than 2.0 | Less than 2.0 | 0.50 ± 0.10 |
| Polymer dispersion | Solid ratio (%) | pH (20°C) | Viscosity (mPa·s) | Density (g/mL) |
| SBR | 44.6 | 8.0–9.0 | 500–1500 | 1.0 |
|
|
Residual mass ratio after passing through a 300 μm sieve.
|