SiC Conversion Coating Prepared from Silica-Graphite Reaction
Figure 7
DSC/TGA results for (a) graphite, SiC-coated graphite prepared (b) at reaction zone (1) and (c) at reaction zone (2) with air blowing (100 mL/min). 10°C/min to 700°C in Ar gas and holding 180 min in air.
(a) |
(b) |
(c) |