A Combined TEM/STEM and Micromagnetic Study of the Anisotropic Nature of Grain Boundaries and Coercivity in Nd-Fe-B Magnets

<div>(a) HRTEM image of four Nd-Fe-B grains separated by <svg height="6.1673pt" id="M85" style="vertical-align:-0.2063904pt" version="1.1" viewbox="-0.0498162 -5.96091 7.39387 6.1673" width="7.39387pt" xmlns="http://www.w3.org/2000/svg" xmlns:xlink="http://www.w3.org/1999/xlink"><g transform="matrix(.013,0,0,-0.013,0,0)"><path d="M536 404C536 423 520 448 491 448C445 448 398 404 308 283L286 338C255 416 242 448 217 448C182 448 138 402 92 341L111 321C149 368 169 378 178 378C188 378 198 363 214 320L254 212C185 117 138 65 107 65C98 65 85 69 82 75C79 82 73 86 65 86C44 86 23 60 23 39C23 7 44 -12 71 -12C119 -12 168 33 265 177L306 61C321 17 347 -12 373 -12C413 -12 465 33 507 96L491 119C459 84 432 60 413 60C395 60 378 92 358 148L321 250C341 279 369 310 389 332C417 363 439 382 456 382C466 382 475 376 481 368C486 361 492 358 496 358C513 358 536 381 536 404Z" id="g113-121"></path><glyph.data ascent="3473" descent="-2876" horiz-adv-x="559" vert-adv-y="559"></glyph.data></g></svg>-, <svg height="9.39034pt" id="M86" style="vertical-align:-3.42943pt" version="1.1" viewbox="-0.0498162 -5.96091 7.65486 9.39034" width="7.65486pt" xmlns="http://www.w3.org/2000/svg" xmlns:xlink="http://www.w3.org/1999/xlink"><g transform="matrix(.013,0,0,-0.013,0,0)"><path d="M556 393C556 426 537 448 514 448C496 448 478 435 471 420C468 414 462 401 466 394C473 382 480 368 480 346C480 268 392 143 338 67H336C329 163 319 253 309 330S286 448 254 448C215 448 160 383 127 337L143 311C167 344 200 373 208 373S222 365 229 320C246 214 264 66 268 -20C219 -83 131 -171 17 -239L25 -261L137 -235C248 -110 273 -79 335 8C384 77 481 215 520 287C544 332 556 363 556 393Z" id="g113-122"></path><glyph.data ascent="3473" descent="-2876" horiz-adv-x="579" vert-adv-y="579"></glyph.data></g></svg>-, and <svg height="6.44133pt" id="M87" style="vertical-align:-0.29774pt" version="1.1" viewbox="-0.0498162 -6.14359 6.59789 6.44133" width="6.59789pt" xmlns="http://www.w3.org/2000/svg" xmlns:xlink="http://www.w3.org/1999/xlink"><g transform="matrix(.013,0,0,-0.013,0,0)"><path d="M475 445L452 468C423 436 401 426 385 426S352 427 305 436C268 443 216 448 185 448C156 448 128 425 102 382C89 360 77 338 64 304L89 291C117 340 143 380 190 380C214 380 268 376 295 373C320 370 344 371 362 374L70 101C32 65 23 36 23 18C23 5 27 -3 31 -8C36 -8 39 -6 42 -1C52 15 67 31 80 40S110 49 143 33C195 8 257 -20 290 -20C339 -20 382 11 439 129L416 148C366 74 334 55 305 55C278 55 236 68 203 81C169 94 141 100 122 96C205 170 348 308 411 376L475 445Z" id="g113-123"></path><glyph.data ascent="3473" descent="-2876" horiz-adv-x="498" vert-adv-y="498"></glyph.data></g></svg>-GBs, (101), (110), and (001) lattice fringes of the grains are visible. (b) HAADF image of the grain, from which the EELS line scans of Figure <a href="../fig9/">9</a> were taken.</div>

Advances in Materials Science and Engineering

fig8

Figure 8

Figure 8: A Combined TEM/STEM and Micromagnetic Study of the Anisotropic Nature of Grain Boundaries and Coercivity in Nd-Fe-B Magnets 