Mechanical and Failure Criteria of Air-Entrained Concrete under Triaxial Compression Load after Rapid Freeze-Thaw Cycles
Figure 1
The failure mode and fracture surface of air-entrained concrete specimen after different freeze-thaw cycles.
(a) Loading direction and surface crack of specimen under triaxial compression load |
(b) Failure mode and surface cracks of air-entrained concrete under triaxial compression after rapid freeze-thaw cycles |
(c) Fracture surface of air-entrained concrete under triaxial compression load after 400 rapid freeze-thaw cycles |