Ageing Effects on Microstructure, Mechanical Properties, and Fracture Behaviour of 9Cr-1.5Mo-1Co-VNbBN Martensitic Steel Welded Joint for High Temperature Application

<div>Light-optical microstructures beneath “type III failure” of CB2 weldment crept at 625°C/80 MPa for 14145 h showing the following: microstructural gradient between WM and FZ (a) and microstructure of FZ in detail (b).</div>

Advances in Materials Science and Engineering

fig12

Figure 12

Figure 12: Ageing Effects on Microstructure, Mechanical Properties, and Fracture Behaviour of 9Cr-1.5Mo-1Co-VNbBN Martensitic Steel Welded Joint for High Temperature Application 

Figure 12 | Ageing Effects on Microstructure, Mechanical Properties, and Fracture Behaviour of 9Cr-1.5Mo-1Co-VNbBN Martensitic Steel Welded Joint for High Temperature Application 