The Performance and Mechanism Analysis of Cement Pastes Added to Aluminum Sulfate-Based Low-Alkali Setting Accelerator
Table 6
Parameters and distribution of pore of cement pastes at 1 d and 28 d.
| Specimens | Curing age/d | Total pore volume/(mL·g−1) | Porosity/% | Pore size distribution/(mL·g−1/%) | 3–20 nm | 20–50 nm | 50–100 nm | >100 nm |
| Blank | 1 | 0.258 | 39.5 | 0.051/19.8 | 0.051/19.8 | 0.106/41.1 | 0.050/19.3 | Y20-S7 | 1 | 0.235 | 35.2 | 0.062/26.4 | 0.038/16.2 | 0.095/40.4 | 0.040/17.0 | Blank | 28 | 0.189 | 29.7 | 0.034/18.0 | 0.070/37.0 | 0.041/21.7 | 0.044/23.3 | Y20-S7 | 28 | 0.161 | 27.1 | 0.023/14.3 | 0.073/45.3 | 0.028/17.4 | 0.037/23.0 |
|
|