Multiaxial Cycle Deformation and Low-Cycle Fatigue Behavior of Mild Carbon Steel and Related Welded-Metal Specimen

Table 4

Fatigue test and analysis results for base-metal and welded-metal specimens.

Strain paths
	(%)	(%)		(MPa)	(MPa)	(%)	(%)	(MPa)
Base-metal fatigue test
UA	0.60	0	0	270	0	0.87	0.16	135	3443
UA	0.60	0	0	273	0	0.87	0.16	137	4012
UA	0.80	0	0	289	0	1.17	0.21	145	1643
UA	0.80	0	0	288	0	1.17	0.21	144	1817
UA	1.03	0	0	302	0	1.51	0.27	151	1257
UA	1.01	0	0	299	0	1.49	0.27	149	1254
IP	0.27	0.50	1.852	194	88	0.63	0.08	119	16269
IP	0.42	0.74	1.762	196	105	0.96	0.11	107	4443
IP	0.42	0.74	1.762	195	107	0.96	0.11	102	4535
IP	0.56	0.96	1.714	214	108	1.26	0.15	119	2929
IP	0.56	0.97	1.732	213	108	1.27	0.15	118	2971
IP	0.71	1.25	1.761	219	111	1.63	0.19	123	1475
IP	0.71	1.18	1.662	218	110	1.58	0.19	117	2053
OP	0.40	0.69	1.725	305	176	0.69	0.17	313	1494
OP	0.40	0.70	1.750	306	170	0.70	0.17	312	1519
OP	0.51	0.85	1.667	326	182	0.81	0.22	322	1002
OP	0.50	0.81	1.620	321	181	0.85	0.22	326	992
OP	0.61	1.01	1.656	336	189	1.01	0.27	336	703
OP	0.61	0.99	1.623	329	186	0.99	0.27	329	642
Welded-metal fatigue test
UA	0.61	0	0	295	0	0.89	0.17	147	289
UA	0.60	0	0	293	0	0.87	0.16	146	432
UA	0.81	0	0	313	0	1.18	0.22	156	118
UA	0.80	0	0	315	0	1.17	0.22	157	177
UA	1.02	0	0	329	0	1.50	0.27	164	70
UA	1.00	0	0	334	0	1.47	0.27	167	60
IP	0.28	0.49	1.750	189	104	0.63	0.08	102	2697
IP	0.42	0.75	1.786	221	121	0.96	0.12	118	1262
IP	0.42	0.74	1.762	220	122	0.97	0.12	120	701
IP	0.57	1.01	1.772	230	131	1.31	0.15	127	384
IP	0.56	1.00	1.786	241	134	1.29	0.15	129	393
IP	0.71	1.25	1.761	253	128	1.63	0.19	142	160
IP	0.70	1.27	1.814	243	129	1.63	0.19	135	145
OP	0.40	0.69	1.725	345	195	0.69	0.18	345	359
OP	0.41	0.68	1.659	335	190	0.68	0.19	335	388
OP	0.49	0.88	1.796	350	198	0.91	0.23	362	220
OP	0.50	0.91	1.820	362	207	0.88	0.24	356	172
OP	0.63	1.03	1.635	405	234	0.88	0.23	390	98
OP	0.56	1.07	1.911	410	237	1.03	0.30	383	76