Effect of Indium Additions on the Formation of Interfacial Intermetallic Phases and the Wettability at Sn-Zn-In/Cu Interfaces
Figure 7
Thickness of the CuZn4 and Cu5Zn8 intermetallic layers at the () interfaces after 60 min at 250°C.