Effect of Material Composition on Cohesion Characteristics of Styrene-Butadiene-Styrene-Modified Asphalt Using Surface Free Energy
Table 1
Properties of neat asphalts.
| Performance | Unit | Binder A | Binder B | Binder C |
| Penetration (25°C, 100 g, 5 s) | 0.1 mm | 85.5 | 84.3 | 87.6 | Softening point (ring ball method) | °C | 45.6 | 48.7 | 47 | Ductility (5 cm/min, 15°C) | cm | >100 | >100 | >100 |
| Residue after aging under rotary film oven (163°C, 85 min) | Loss of quality | % | 0.07 | 0.18 | 0.12 | Penetration ratio | % | 70 | 64 | 61 | Ductility (5 cm/min, 10°C) | cm | 9.0 | 6.5 | 8.0 |
|
|