Experimental Investigation of Polyurea-Coated Steel Plates at Underwater Explosive Loading

<table class="table-group" id="tab2"><tr><td><table class="table"><tr><td class="thead-hr" colspan="3"><hr/></td></tr><tr class="thead"><td class="align_left">Sample</td><td class="align_center">Tensile strength (MPa)</td><td class="align_center">Fracture elongation (%)</td></tr><tr><td class="thead-hr" colspan="3"><hr/></td></tr><tr><td class="align_left">Polyurea</td><td class="align_center">18.1</td><td class="align_center">184</td></tr><tr class="table-tr"><td colspan="3"><hr class="tbody-hr"/></td></tr></table></td></tr></table>

<div>Physical and mechanical properties of polyurea used in blast tests.</div>