High- and Low-Temperature Properties and Thermal Stability of Silica Fume/SBS Composite-Modified Asphalt Mortar
Table 1
Indicators of raw materials.
| Materials | Property | Value |
| Matrix asphalt | Penetration (25°C, 0.1 mm) | 83 | Ductility (15°C, cm) | >100 | Softening point (°C) | 46 | Penetration index | −1.4 | Dynamic viscosity (60°C, Pa·s) | 175 | Density (g/cm3) | 1.004 |
| SBS | Block ratio | 30/70 | Tensile strength (MPa) | 21.6 | Elongation at break (%) | 850 | Relative molecular mass | 28 × 104 |
| Silica fume | Appearance | Grey | SiO2 content (%) | >92 | pH | 6∼8 | Particle size distribution (μm) | 0.1∼0.3 | Granularity (mesh) | 300∼500 | Loose density (g/cm3) | 0.1∼0.2 | Tight heap density (g/cm3) | 0.3∼0.4 | Specific surface area (m2/g) | >25 | Burning loss (%) | <5 | Impurity content (%) | <8 | Water content (%) | <5 |
|
|