Research Article
Study of Thermomechanical Properties of an Al-Zn-Based Composite Reinforced with Dodecaboride Particles
Figure 5
Brinell hardness after TMA for 0 wt.% B (light gray), 2.08 wt.% B (light-dark gray), and 4.17 wt.% B (dark gray) at 125°C, 160°C, and 200°C for (a) 5 wt.% Zn and (b) 10 wt.% Zn.
(a) |
(b) |