Change of Parameters of the Koiwa–Hasiguti Dynamic Dislocation Relaxation in Nanostructured and Polycrystalline Zirconium after Severe Plastic Deformation and Annealing
Figure 1
Temperature dependences of the logarithmic decrement in zirconium samples with the different mean grain size : 1-Zr-CG, = 150 μm; 2-Zr-HEA, = 12 μm; 3-Zr-HEAD, = 2 μm; 4-Zr-0, = 392 nm; 5-Zr-01, = 117 nm; 6-Zr-02RT, = 113 nm; 7-Zr-02CE, = 100 nm.