Low-Temperature Brazing of Titanium Using Al-Based Filler Alloys
Table 8
Ti/Ti–Ti/Al-brazed joints using Al–Ag-type filler alloys.
| References | Materials | Conditions | Bonding | Shear strength (MPa) | Intermetallic compounds at Ti/filler interface | Parent 1 | Parent 2 | Filler | Type | Thickness/gap width () | Temperature (°C) | Time (min) |
| [28] | Pure Ti | Al (3003) | Al–20Ag–10Cu | 100 | Vacuum | 600 | 5 | ∼38 | | [29] | Pure Ti | Al (3003) | A1–33Ag | 100 | Vacuum | 630 | 3 | | | [30] | Ti Grade 5, 2 | Ti Grade 5, 2 | Al–38Ag–7.4Si–0.6Fe | 260 | Vacuum/torch with flux | >580 liquidus temperature | | Poor result | | [3] | Ti Grade 2 | Ti Grade 2 | Al–28Ag | Powder +325/−100 mesh | Vacuum/torch with flux | 600–620 | | 70 | | Al–28.5Ag–21Cu–1.3Mg | 260 | 650–710 | | 67.6 | |
|
|
Another undetermined very thin one. |