Low-Temperature Brazing of Titanium Using Al-Based Filler Alloys
Table 9
Ti/Ti-brazed joints using Al–Ni- and Al–Mn-type filler alloys.
| References | Materials | Conditions | Bonding | Shear strength (MPa) | Intermetallic compounds at Ti/filler interface | Parent 1 | Parent 2 | Filler | Type | Thickness/gap width () | Temperature (°C) | Time (min) |
| [29] | Pure Ti | Pure Ti | Al–1Mn, Al–1Ni | 100 | Vacuum | 680 | 3 | | | [30] | Ti Grade 5, 2 | Ti Grade 5, 2 | TiBraze Al-700 (Al–21.5Ni–9Cu–9.6Si–1.3Fe–0.6Mn) | 300 | Vacuum/torch with flux | ≥607 | | 93 in vacuum and poor result by torch | , | [3] | Ti Grade 5, 2 | Ti Grade 5, 2 | TiBraze Al-700 (Al–21.5Ni–9Cu–9.6Si) | 290 | Vacuum/torch with flux | 700–720 | | 127.3 G5 81.6 G2 | , | Cited in [2] | Ti Grade 5 | Ti Grade 5 | Al–1.2Mn–0.6Si–0.7Fe–0.2Cu | | | >660 | | 89 | |
|
|