Nanoindentation Hardness Distribution and Strain Field and Fracture Evolution in Dissimilar Friction Stir-Welded AA 6061-AA 5A06 Aluminum Alloy Joints

<table class="table-group" id="tab2"><tr><td><table class="table"><tr><td class="thead-hr" colspan="4"><hr/></td></tr><tr class="thead"><td class="align_left">Samples</td><td class="align_center">RS (rpm)</td><td class="align_center">TS (mm/min)</td><td class="align_center">RS/TS (r/mm)</td></tr><tr><td class="thead-hr" colspan="4"><hr/></td></tr><tr><td class="align_left">Sample 1</td><td class="align_center">600</td><td class="align_center">150</td><td class="align_center">4</td></tr><tr><td class="align_left">Sample 2</td><td class="align_center">900</td><td class="align_center">150</td><td class="align_center">6</td></tr><tr><td class="align_left">Sample 3</td><td class="align_center">1200</td><td class="align_center">150</td><td class="align_center">8</td></tr><tr><td class="align_left">Sample 4</td><td class="align_center">600</td><td class="align_center">100</td><td class="align_center">6</td></tr><tr><td class="align_left">Sample 5</td><td class="align_center">900</td><td class="align_center">100</td><td class="align_center">9</td></tr><tr><td class="align_left">Sample 6</td><td class="align_center">1200</td><td class="align_center">100</td><td class="align_center">12</td></tr><tr class="table-tr"><td colspan="4"><hr class="tbody-hr"/></td></tr></table></td></tr></table>

<div>Investigated welding parameters in experimental scale-up processing.</div>

Advances in Materials Science and Engineering

tab2

Table 2

Table 2: Nanoindentation Hardness Distribution and Strain Field and Fracture Evolution in Dissimilar Friction Stir-Welded AA 6061-AA 5A06 Aluminum Alloy Joints 

Table 2 | Nanoindentation Hardness Distribution and Strain Field and Fracture Evolution in Dissimilar Friction Stir-Welded AA 6061-AA 5A06 Aluminum Alloy Joints 