Characterization of Esthetic Orthodontic Wires Made from Glass-Fiber-Reinforced Thermoplastic Containing High-Strength, Small-Diameter Glass Fibers
Table 4
Flexural properties of GFRTPs after thermocycling.
| | 0 cycles | 600 cycles | 1200 cycles | Strength (MPa) | Modulus (GPa) | Strength (MPa) | Modulus (GPa) | Strength (MPa) | Modulus (GPa) |
| GFRTP-13 | 958.5 ± 137.4a,b | 35.0 ± 5.2a | 938.9 ± 102.2 | 34.5 ± 5.6 | 913.3 ± 122.1a | 35.4 ± 5.9 | GFRTP-7 | 1120.1 ± 197.0a | 40.5 ± 9.2 | 1037.0 ± 123.2 | 39.7 ± 6.9 | 999.2 ± 56.8 | 38.4 ± 6.5 | GFRTP-5 | 1126.2 ± 92.5b | 42.6 ± 5.3a | 1043.5 ± 81.5 | 40.0 ± 3.6 | 1060.4 ± 102.4a | 38.3 ± 5.9 |
|
|
Mean values with the same superscripts are significantly different from each other ( ). |