Coexistence of Two Cubic-Lattice Co Matrices at High Temperatures in Co-Re-Cr-Ni Alloy Studied by Neutron Diffraction

Table 1

Composition of the fcc Co matrix measured on the Co-17Re-23Cr-25Ni alloy by EDS at positions marked by + in Figure 4.

Heat treatment	Co	Re	Cr	Ni
ST	35.50	16.85	23.91	23.74
ST + 100 hours at 800°C	38.22	12.18	21.97	27.63