Effects of Gd211 Particles Characteristic in the Precursor Pellets on the Levitation Force of Single-Domain GdBCO Bulks Prepared by the Gd + 011 TSIG Method

<div>The SEM pictures of the PSPP with the same initial new solid phase (Gd2O3 + 011) sintered at different temperatures (a) 25°C (unsintered), (b) sintered at 950°C, (c) 1000°C, (d) 1050°C, (e) 1100°C, (f) 1150°C, and (g) 1200°C.</div>

Advances in Materials Science and Engineering

fig3

Figure 3

Figure 3: Effects of Gd211 Particles Characteristic in the Precursor Pellets on the Levitation Force of Single-Domain GdBCO Bulks Prepared by the Gd + 011 TSIG Method 

Figure 3 | Effects of Gd211 Particles Characteristic in the Precursor Pellets on the Levitation Force of Single-Domain GdBCO Bulks Prepared by the Gd + 011 TSIG Method 