Joining of Cf/SiC Ceramic Matrix Composites: A Review
Table 3
Self-joining of Cf/SiC composites using metal filler (SS = shear strength).
| CMCs | Basic information | Metal filler | Process parameters | Bend strength (MPa) | Ref. |
| Cf/SiC | CVD-SiC | Ti | 1700°C, 3 min, 60 MPa, vacuum | 24.6 (SS) | [48] | Cf/SiC | 3D, 10.0 vol.%, PIP | Cu-Au-Pd-V | 1170°C, 10 min, 1.5 × 10−3 Pa | 135 | [59] | Cf/SiC | 3D | Pd-Co-V | 1250°C, 20 min, 3.0–7.0 × 10−3 Pa | — | [60] | Cf/SiC | 3D, PIP, 10.0 vol.% | Cu-Pd-V | 1170°C, 10 min, 3.0–7.0 × 10−3 Pa | 128 | [61] |
|
|