Uneven Precipitation Behavior during the Solutionizing Course of Al-Cu-Mn Alloys and Their Contribution to High Temperature Strength
Table 2
Tension properties at 25°C and 300°C of the A2 alloy at different states.
| State | | UTS (MPa) | YS (MPa) | Elongation (%) |
| As-cast | 25°C | 147 ± 9.0 | 90 ± 4.0 | 4.5 ± 0.7 | 300°C | 89 ± 8.0 | 68 ± 5.0 | 6 ± 0.5 |
| As-solutionized | 25°C | 256 ± 18.0 | 157 ± 1.6 | 4.8 ± 0.7 | 300°C | 115 ± 6.0 | 93 ± 2.6 | 6.04 ± 2.1 |
| T6 | 25°C | 369 ± 22.0 | 248 ± 4.5 | 6.26 ± 0.8 | 300°C | 116 ± 11.0 | 96 ± 8.0 | 8.3 ± 4.5 |
|
|